Increasing the Sodium Content in P2-Type Layered Oxides As Cathode Materials for Sodium-Ion Batteries
Mingfeng Xu,Matteo Bianchini
DOI: https://doi.org/10.1149/ma2023-024556mtgabs
2023-12-22
ECS Meeting Abstracts
Abstract:P2-type layered oxides exhibit superior Na ion conductivity and structural stability compared to their O3 analogues, making them promising candidate materials for next generation batteries. However, their lower initial Na contents (Na/transition metals < 1) restrict their capacity during the first charge process, and the transitions between P- and O2-type structures during cycling further deteriorate their stability. [1,2] Our work aims to increase the Na inventory in pristine cathode compositions, especially relevant for full cell systems, while maintaining their cycling stability. We started with the well-studied P2 material Na 2/3 Ni 1/3 Mn 2/3 O 2 and have worked on incorporating Li in the transition metal layers to stabilize the structure, while at the same time increasing the Na content. [3,4] In this respect, a great challenge is to control the phase formation during the synthesis. When the Na content exceeds a certain limit, an O3 structure is more likely to form than a P2 structure. [1] On the other hand, at too low temperatures, a P3 polymorph is preferred. [5] By regulating the synthesis conditions, Na contents have been successfully increased in a series of materials between two end compositions, Na 2/3 Ni 1/3 Mn 2/3 O 2 and Na 5/6 Li 5/18 Mn 13/18 O 2 . In this presentation, we report on unpublished in situ XRD characterizationsof these compositions during their solid-state synthesis, as well as on their crystal structures and electrochemical behavior, which involves varying amount of Ni redox. These time-resolved studies of structural evolutions provide guidance for further synthesis of desired phases and compositions. Along with the electrochemical results, we also aim to answer the questions on the charge compensation mechanisms that sustain the electrochemical performance as the amount of Li increases and Ni decreases. Finally, we also explore which amount of Li substitution can best balance the structural stability and capacity retention of the cathode material. References [1] C. Zhao, Q. Wang, Z. Yao, J. Wang, B. Sánchez-Lengeling, F. Ding, X. Qi, Y. Lu, X. Bai, B. Li, H. Li, A. Aspuru-Guzik, X. Huang, C. Delmas, M. Wagemaker, L. Chen, Y.-S. Hu, Science 2020 , 370 , 708–711. [2] D. H. Lee, J. Xu, Y. S. Meng, Phys. Chem. Chem. Phys. 2013 , 15 , 3304. [3] T. Jin, P. Wang, Q. Wang, K. Zhu, T. Deng, J. Zhang, W. Zhang, X. Yang, L. Jiao, C. Wang, Angew. Chem. Int. Ed. 2020 , 59 , 14511–14516. [4] J. Xu, D. H. Lee, R. J. Clément, X. Yu, M. Leskes, A. J. Pell, G. Pintacuda, X.-Q. Yang, C. P. Grey, Y. S. Meng, Chem. Mater. 2014 , 26 , 1260–1269. [5] M. Bianchini, J. Wang, R. J. Clément, B. Ouyang, P. Xiao, D. Kitchaev, T. Shi, Y. Zhang, Y. Wang, H. Kim, M. Zhang, J. Bai, F. Wang, W. Sun, G. Ceder, Nat. Mater. 2020 , 19 , 1088–1095.