Preparation of Er:YAG Crystal-Derived All-Glass Silica Fibers For a 1550-nm Single-Frequency Laser
Yongyao Xie,Zhenhua Cong,Zhigang Zhao,Xingyu Zhang,Xian Zhao,Wei Zhao,Xianbin Shao,Zhaojun Liu
DOI: https://doi.org/10.1109/jlt.2021.3076889
IF: 4.7
2021-07-01
Journal of Lightwave Technology
Abstract:YAG crystal-derived all-glass silica fibers (YDSFs) with different doping concentrations of Er3 were fabricated using the molten-core method. A maximum gain coefficient of 1.46 dBcm was obtained when an Er:YAG rod at a doping concentration of 5 at. was used as the precursor material. To the best of our knowledge, this is the highest gain coefficient at the 1.5-m band in similar YDSFs. The diffusion between the Er:YAG core and silica cladding was investigated during the whole preparation process. Based on the homemade Er3-doped YDSF, a 1.55-m pulsed single-frequency YDSF laser was demonstrated for the first time, delivering an output power of 24.2 mW when the absorbed pump power was 174 mW. The corresponding slope efficiency was 15.1. A single-pulse energy of 32.7 nJ was obtained with a pulse duration of 78 ns and a repetition rate of 739 kHz. The signal-to-noise ratio was higher than 75 dB.
engineering, electrical & electronic,optics,telecommunications