Abstract:Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly attractive for high-field applications, especially in particle accelerator magnets, nuclear magnetic resonance spectrometers, medical magnetic resonance imaging systems and nuclear fusion reactors. Herein, through an industrially scalable and cost-effective manufacturing strategy, a practical level critical current density up to 1.1x10^5 A/cm2 at 4.2 K in an external magnetic field of 10 T was achieved in Cu/Ag composite sheathed Ba0.6K0.4Fe2As2 superconducting tapes. The preparation strategy combines flat rolling to induce grain texture and a subsequent hot-isostatic-pressing densification. By varying the parameters of rolling, the degree of grain texture was engineered. It is found that the transport properties of the Ba1-xKxFe2As2 tapes can be enhanced by applying a large amount of deformation during rolling, which can be attributed to the improved degree of c-axis texture. Microstructure characterizations on the highest-performance tape demonstrate that the Ba1-xKxFe2As2 phase has a uniform element distribution and small grains with good connectivity. Grain boundary pinning is consequently enhanced as proved by large currents circulating through the sample even at 25 K. Our work proves that Cu/Ag composite sheathed Ba1-xKxFe2As2 superconducting tapes can be a promising competitor for practical high-field applications in terms of the viable, scalable and cost-effective fabrication strategy applied and the high transport properties achieved in this work.

Fabrication and Properties of Aligned Sr0.6k0.4fe2as2 Superconductors by High Magnetic Field Processing

High-performance Ba1-xKxFe2As2 superconducting tapes with grain texture engineered via a scalable and cost-effective fabrication

Anisotropic Structural And Magnetic Properties Of The Field-Aligned Superconducting System Smfeaso1-Xfx (X=0, 0.1, 0.2, 0.25 And 0.3)

Fabricating Ba0.5Cs0.5Fe2As2 Films on BaFe2As2 Substrates and Their Superconducting Properties

Strongly enhanced current densities in Sr0.6K0.4Fe2As2 superconducting tapes

High Upper Critical Field of Sm0.85Nd0.15FeAsO0.85F0.15 Superconductors by Mechanical Alloying Synthesis

A Possible New Parent Compound Sr4al2o6fe2as2 with High-T-C Superconductivity

Approaching the ultimate superconducting properties of (Ba,K)Fe2As2 by naturally formed low-angle grain boundary networks

Realization of epitaxial thin films of the superconductor K-doped Ba Fe 2 As 2

Observation of reversible critical current performance under large compressive strain in Sr0.6K0.4Fe2As2 tapes

Anisotropic Superconducting Properties of the Aligned Sm0.95la0.05feaso0.85f0.15 Microcrystalline Powder

Biaxial Alignment of High-Tc Superconductor Polycrystals(Iii) - Demonstration in A Bi-2212(Yb) Thick-Film

Transport and Anisotropy in Single-Crystallinesrfe2as2anda0.6

Fabrication and Transport Properties of 100 m Class Sr0.6K0.4Fe2As2 Wires and Pancake Coils

Strengthened proximity effect at grain boundaries to enhance inter-grain supercurrent in Ba1-xKxFe2As2 superconductors

High, Magnetic Field Independent Critical Currents In (Ba,K)Fe2as2 Crystals

Tailoring the Critical Current Properties in Cu-sheathed Sr1−xKxFe2As2superconducting Tapes

Low-temperature Transport Properties of Doped Ba0.57K0.43Fe2As2 Superconductors in High Magnetic Field

Low field anomaly in the critical current of Ba1‐xKxFe2As2 tapes

High transport Jc in magnetic fields up to 28 T of stainless steel/Ag double sheathed Ba122 tapes fabricated by scalable rolling process

Upper Critical Field, Anisotropy, And Superconducting Properties Of Ba1-Xkxfe2as2 Single Crystals