Roles Of L1(0) Ordering In Controlling The Magnetic Anisotropy And Coercivity Of (111)-Oriented Copt Ultrathin Continuous Layers In Copt/Aln Multilayer Films

Wupeng Cai,Ji Shi,Yoshio Nakamura,Wei Liu,Ronghai Yu

DOI: https://doi.org/10.1063/1.3650243

IF: 2.877

2011-01-01

Journal of Applied Physics

Abstract:Chemical ordering of (111)-oriented CoPt ultrathin continuous layers in CoPt/AlN multilayer structure has been investigated. It is found that upon thermal annealing at 600 degrees C, CoPt layers undergo ordering transformation even when the CoPt layers are as thin as 2 nm. The degree of ordering increases with increasing the layer thickness. For the 600 degrees C annealed CoPt/AlN multilayer film with 2 nm thick CoPt layers, due to the ordering, out-of-plane coercivity is increased to 3330 Oe, while large perpendicular magnetic anisotropy constant of 8.1 x 10(6) erg/cm(3) is exhibited. These coercivity and anisotropy energy are appropriate for the practical use as magnetic recording media. It is clear that for such a structure, ordering transformation does not impair the perpendicular magnetic anisotropy induced by the interface and magnetoelastic effects. The easy axis of magnetization still lies in the layer normal direction, i.e., [111] direction, although for L1(0) structure it is supposed to lie in the [001] direction. But L10 ordering does contribute to the enhancement of coercivity. (C) 2011 American Institute of Physics. [doi: 10.1063/1.3650243]