Effect of Trace Rare-Earth Ce on Microstructures and Mechanical Properties of Al-Cu5 Alloy

ZHU Tao,ZHU Wei-dong,ZHOU Fang,JIA Yi-wang,TIAN Qin

2011-01-01

Abstract:Al-Cu5 alloys with different Ce additions of 0, 0.05%, 0.10%, 0.15% and 0.20% were prepared. The influence of trace Ce on the microstructures and mechanical properties of as-cast and heat treated Al-Cu5 alloys were investigated by optical microscope and mechanical test. The results show that under the same heat treatment condition the effect of Ce on the microstructure and mechanical properties of Al-Cu5 alloy depended remarkably on the as-cast microstructure of the alloy. When the addition of Ce was 0.10%, the combination effects of purifying, refining and micro-alloying of Ce on the alloy became remarkable, the tensile strength and elongation of the as-cast and heat-treated alloys reached maximum at the same time, which are 180.1 MPa, 8.8% and 387.4 MPa, 7.9%, respectively. In the microstructure of as-cast alloy with 0.1% Ce addition, there are a little dot-like precipitates with uniform size; the twig-like eutectics became short and thin and distributed dispersively.