Charge Compensation Effect In Pr1-Ysryfe1-Xcoxaso Codoped With Sr And Co

Xiao Lin,Hanjie Guo,Chenyi Shen,Yongkang Luo,Qian Tao,Guanghan Cao,Zhuan Xu

DOI: https://doi.org/10.1103/PhysRevB.83.014503

IF: 3.7

2011-01-01

Physical Review B

Abstract:Superconductivity of polycrystalline Sr and Co codoped Pr1-ySryFe1-xCoxAsO samples was investigated by measuring resistivity, dc magnetic susceptibility, thermopower, and Hall effect. In the PrFe1-xCoxAsO samples with only Co doping, T-c reaches a maximum of 16 K at x = 0.075-0.1, and the variation of Tc with Co content (x) is a dome-shaped curve. In the Co and Sr codoped Pr0.8Sr0.2Fe1-xCoxAsO system, the phase diagram separates into two regions. The thermopower and Hall data indicate that the hole-type charge carrier dominates in the low Co doping region (x <= 0.075) and the system becomes electron type in the high Co doping region (x >= 0.075). T-c first decreases with increasing Co content to a lowest T-c of 3.5 K at x = 0.075, then it increases and reaches a maximum of similar to 16 K at x = 0.15. The transition from hole-type to electron-type superconductivity in the nominal Pr0.8Sr0.2Fe1-xCoxAsO system around x = 0.075 implies that the charge-carrier density is one of the decisive factors to control superconductivity.