Abstract:The (1 − x)(Li 0.03 Na 0.5 K 0.47 )(Nb 0.92 Sb 0.05 Ta 0.03 )O 3 –xBa 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (LNKNST–BCZT, x = 0, 0.5, 1.5, 2.5, and 3.5%) lead-free piezoceramics were synthesized by the conventional solid-state reaction method with adding nano-sized Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (BCZT) powder to investigate their influences on crystal structure and electrical properties. The X-ray diffraction (XRD) analysis reveals that all the sintered LNKNST–BCZT ceramics exhibit pure perovskite structure with the mainly rhombohedral (R) phase or the coexistence of rhombohedral (R) phase and tetragonal (T) phase. The composition of the LNKNST–1.5%BCZT ceramics locates around the critical point, i.e., the ceramics changing from the coexistence of rhombohedral (R) phase and tetragonal (T) phase to purely rhombohedral (R) phase, and presents the most densified microstructure morphology, which can be confirmed further by the field emission scanning electron microscope (FESEM) observation. There are two dielectric anomalies in the temperature dependent dielectric properties curves of the LNKNST–BCZT ceramics, which correlate with the ferroelectric rhombohedral (R) phase changing to the ferroelectric tetragonal (T) phase, and then to the paraelectric cubic (C) phase. Both the Curie–Weiss law and the power law fittings confirm the diffuse phase transition ferroelectrics characteristic of the LNKNST–1.5%BCZT ceramics, which is considered as correlating with the polar nanoregions (PNRs). Due to the densification effect caused by the chosen amount of nano-sized BCZT doping and the construction of R–T polymorphic phase boundary, the LNKNST–1.5%BCZT ceramics exhibit the best ferroelectric and piezoelectric properties. The complex impedance spectroscopy analysis confirms that the extrinsic electrical conduction mechanism at high temperatures is dominated by the oxygen vacancies induced by the evaporation of the alkali metals during sintering.

Effect of the Addition of CaZrO3 and LiNbO3 on the Phase Transitions and Piezoelectric Properties of K0.5Na0.5NbO3 Lead‐Free Ceramics

Effects of Na Excess on the Preparation and Characterization of (K0.5na0.5)nbo3ceramics

Effects of nano-sized BCZT on structure and electrical properties of KNN-based lead-free piezoceramics

New K0.48Na0.52NbO3–Bi(Zn0.5Zr0.5)O3 Lead-Free Ceramics: Microstructure and Piezoelectricity

Preparation of KNN Based Lead-Free Piezoelectric Ceramics Via Composition Designing and Two-Step Sintering

(Bi0.5na0.5)(zr0.97w0.01fe0.02)o3 Doping Effects on KNN‐based Lead‐free Ceramics Prepared Via Two‐step Sintering Technique

Microstructure and electrical properties of (K0.48Na0.52)0.97Li0.03NbO3 - 0.03CaZrO3 lead-free piezoceramics with (4CuO–TiO2–2Nb2O5) additive

Electrical Performance and Conduction Mechanism of Potassium Sodium Niobate-Based Lead-Free Piezoceramics Via Two-Step Sintering Route

Phase Structure and Electrical Properties of (Li,ta)-Doped (k,na)nbo3 Lead-Free Piezoceramics in the Vicinity of Na/K = 50/50

A high temperature stable piezoelectric strain of KNN-based ceramics

Effects of the Addition of Li0.8Ni0.2Nb0.96O3 on the Structure and Electrical Properties of K0.48Na0.52NbO3 Lead-Free Piezoceramics

Enhanced piezoelectric properties in 0.96(K0.48Na0.52)(Nb1−xTax)O3–0.04(Bi0.5Ag0.5)ZrO3 lead-free ceramics

Phase Structure and Polar Characteristics of Alkali Niobate Ceramics Modified by Ba0.6ca0.4zro3

Ca2+ Doping Effects in (K, Na, Li)(Nb0.8Ta0.2)O3 Lead-Free Piezoelectric Ceramics

Effects of the Co-Addition of Li, Sb, Ta on the Phase Structure and Piezoelectric Properties of (Na, K) NbO3 Lead Free Piezoceramics

Polymorphic Phase Transition And Enhanced Piezoelectric Properties Of Litao3-Modified (Na0.52k0.48) (Nb0.93sb0.07)O-3 Lead-Free Ceramics

Relationship Between Phase Structure and Electrical Properties of (k0.5na0.5)nbo3–litao3 Lead-Free Ceramics

Piezoelectric Properties and Temperature Sensitivity for CaZrO3 Doped KNN-based Ceramics Sintered in Reducing Atmosphere

Enhancement of piezoelectric properties and temperature stability by forming an MPB in KNN-based lead-free ceramics

Improving densification and electrical properties of KNN-based lead-free piezoceramics via two-step sintering method

Polymorphic phase transition and enhanced piezoelectric properties of LiTaO<sub>3</sub>-modified (Na<sub>0.52</sub>K<sub>0.48</sub>) (Nb<sub>0.93</sub>Sb<sub>0.07</sub>)O<sub>3</sub>lead-free ceramics