Abstract:In this study, a systematic research has been conducted into the powder modification mechanism, the effects of binder compositions on the thermal behavior, and the mechanical properties of the ceramic injection molded system. SA is adopted to modify the as-received ceramic powder for the ceramic injection molding system. The TGA results demonstrate that the mass loss in SA occurs at 200–300°C while the loss in SA-modified zirconia is mainly located at 300–400°C, which is believed that SA reacts with zirconia through an esterification reaction, causing the exothermic peak to shift to a higher temperature. TGA analysis at different locations on the green bodies can effectively evaluate the CIM binder segregation and it is observed that, for feedstock B30, there are four data points in the defined sensitivity range, which could be proved to be the most homogeneous. And it has the best mechanical performance, with three-point flexural strength of 825.7MPa and the relative density of 98.8%. Feedstock B60 has the maximum pores and the minimum mechanical strength, with the relative density of 95.1% and the three-point flexural strength of 541.4MPa. The Weibull modulus for Feedstock B30 is greater than 10, signifying the most concentrated strength distribution, which further verifies that feedstock B30 is the most homogeneous formula.

Surface Modification Mechanism of Stearic Acid to Zirconia Powders Induced by Ball Milling for Water-Based Injection Molding

Surface Modification of the Zirconia Powders for Injection Molding

Surface Modification and Water Debinding in Zirconia Powder Injection Molding

Novel Fabrication of More Homogeneous Water-Soluble Binder System Feedstock by Surface Modification of Oleic Acid

Injection Molding of Zirconia Ceramics Using Water-Soluble Binder

Surface Modification of Alumina Powder Particles Through Stearic Acid for the Fabrication of Translucent Alumina Ceramics by Injection Molding

A Strategy to Obtain a High-Density and High-Strength Zirconia Ceramic Via Ceramic Injection Molding by the Modification of Oleic Acid

Effect of surface modification on zirconia ceramic injection molding

Surface Modification of Ceramic Powders by Titanate Coupling Agent for Injection Molding Using Partially Water Soluble Binder System

Modification Mechanism of the Zta Ceramic Powders with Stearic Acid

Injection molding of surface modified powders with high solid loadings: A case for fabrication of translucent alumina ceramics

Powder Modification Mechanism, Effects of Binder Compositions on the Thermal Behavior, and the Mechanical Properties of the Ceramic Injection Molded System

Water Debinding for Zirconia Powder Injection Molding

Solvent Debinding Behavior of Zirconia Powder Injection Molding

The thermal debinding of soluble binders in injection molded zirconia ceramic from room temperature to 250°C

The Effect of Organic Vehicle on the Injection Molding of Ultra-Fine Zirconia Powders

Influence of Surfactant Addition on Rheological Behaviors of Injection-Molded Ultrafine 98W-1Ni-1fe Suspension

Surface Modification of Domestic Zirconia Powder

Surface-modified by coupling agent and injection molding of zirconia powder

Study Of Water-Debinding For Ceramic Parts By Injection Molding

The effects of surfactants on CIM of Si3N4