Photoluminescence Characteristics of Na4Ca3(AlO2)10∶Eu2+,Mn2+

WANG Xue,TIAN Lian-hua

DOI: https://doi.org/10.3788/fgxb20113211.1109

2011-01-01

Abstract:A novel phosphor Na4Ca3(AlO2)10∶Eu2+ was prepared by solid state reaction method in a thermal-carbon reducing atmosphere.The photoluminescence(PL) properties were investigated in this paper.The excitation spectrum of Na4Ca3(AlO2)10∶Eu2+ showed two absorption bands centered at 262 nm and 320 nm respectively.The photoluminescence spectrum of Na4Ca3(AlO2)10∶Eu2+ exhibited a single emission peak centered at 441 nm,which could be attributed to 5d-4f transition of Eu2+.The excitation spectrum of Na4Ca3-(AlO2)10∶Mn2+ showed absorption peak at about 440 nm monitoring at 542 nm,which shows spectral overlap between emission spectrum of Na4Ca3(AlO2)10∶Eu2+.Co-doped Mn2+ with Eu2+,the photoluminescence spectra of Na4Ca3(AlO2)10∶Eu2+,Mn2+ were observed two peaks centered at 441 nm and 542 nm correspon-ding to the 5d-4f transition of Eu2+ and the d-d transition of Mn2+,respectively.With increasing the concentration of Mn2+,the emission intensity of 5d-4f transition of Eu2+ at 441 nm was significantly decreased,whereas the d-d transition of Mn2+ at 542 nm was found to increase.The decay lifetime for Eu2+ was found to decrease with increasing Mn2+ dopant content,which was strong evidence for the energy transfer from Eu2+ to Mn2+.We were also interested in investigating the energy transfer efficiency ηT of Eu2+→Mn2+.With increasing Mn2+ dopant content,the energy transfer efficiency ηT was found to increase gradually.According to the Dexter's energy transfer formula of multipolar interaction,it was demonstrated that the energy transfer from Eu2+ to Mn2+ was due to the electric quadripole-quadripole interaction of the resonance transfer.According to the CIE chromaticity coordinates of Na4Ca3(AlO2)10∶Eu2+,xMn2+,it was clearly observed that the CIE chromaticity coordinates with the increase of Mn content shifted from blue region to white region.