Emissions of 1.20 and 1.38 μm from Ho3+-doped lithium-barium-bismuth-lead oxide glass for optical amplifications

Bo Zhou,Dianlai Yang,Hai Lin,Edwin Yue-Bun Pun

DOI: https://doi.org/10.1016/j.jnoncrysol.2010.11.056

IF: 4.458

2011-01-01

Journal of Non-Crystalline Solids

Abstract:Efficient infrared emissions at 1.20μm [5I6→5I8 transition] and 1.38μm [(5F4, 5S2)→5I5 transition] from Ho3+-doped lithium–barium–bismuth–lead (LBBP) glass were observed. The stimulated emission cross-sections were calculated to be 0.29×10−20 and 0.25×10−20cm2 for 1.20 and 1.38μm emissions, respectively. Judd-Ofelt characteristic parameters Ω2, Ω4 and Ω6 for Ho3+ in LBBP glass were calculated to be 6.72×10−20, 2.35×10−20 and 0.61×10−20cm2, respectively, which indicates a strong asymmetry and a covalent environment between the Ho3+ ions and the ligands in this glass. The optical amplifications operating at these relatively unexplored wavelength regions were evaluated and discussed.