Abstract:The all-composite sandwich structure with the honeycomb core is a lightweight and high-strength structure with broad application scenarios. The face sheet and honeycomb core of the proposed all-composite sandwich structure in this work are composed of carbon-fiber-reinforced polymer (CFRP) composites. The mechanical response and damage mechanism of the all-composite sandwich structure under out-of-plane quasi-static compression and out-of-plane impact are studied by numerical methods. The refined finite element models of the sandwich structures are built on the ABAQUS/Explicit platform. The micromechanics of failure (MMF) theory based on physical component failure is used to describe the intralaminar damage mechanism of the face sheet and honeycomb core, and the mixed-mode exponential cohesive zone model (ECZM) is utilized to simulate the initiation and evolution of interlayer damage. In addition, the cohesive contact approach is adopted to capture the debonding failure at the face-sheet/core. The numerical results show that the all-composite sandwich structure has the characteristics of large structural stiffness and strong energy absorption ability. The failure mechanism of the all-composite sandwich structure under compression is mainly matrix damage and delamination of the honeycomb core, with buckling and folding in appearance. Under out-of-plane impact, matrix damage and delamination arise on the upper sheet, little damage is observed on the lower sheet, and the delamination damage morphology tends to be circular with increasing impact energy. In addition, the interface failure of the upper-sheet/core is more than that of the lower-sheet/core. In addition, the matrix damage near the impact center of the honeycomb core tends to be consistent with the delamination contour, and a small amount of fiber failure is also observed, which manifests as a collapse morphology of the impact area. The research results enrich the understanding of the mechanical behavior of all-composite sandwich structures with honeycomb cores and provide theoretical support for their potential applications.

Study on the residual strength of metal honeycomb sandwich structure with typical defects

Study on Coplanar Mechanical Properties of Metal Honeycomb Sandwich with Typical Defects

Study on Three-Point Bending Mechanical Performance of Thin-Walled Super Alloy Honeycomb Sandwich with Penetrable Defects

Study on Aluminum Honeycomb Sandwich Panels with Random Skin/Core Weld Defects

Compression Performance of Composite Honeycomb Sandwich Structures with Prefabricated Defects

Damage sensitivity studies of composite honeycomb sandwich structures under in-plane compression and 4-point bending: experiments and numerical simulations

Effect of Defect on the Compressive Response of Sandwich Structures with Carbon Fiber Pyramidal Truss Cores

Study on damage failure for a new double-triangular truss core sandwich structure

STRENGTH INVESTIGATION OF COMPOSITE HONEYCOMB STRUCTURES AFTER REPAIR

Effect of void defects on mechanical behavior and failure features of C/C honeycomb structure

Numerical Studies on Failure Mechanisms of All-Composite Sandwich Structure with Honeycomb Core under Compression and Impact Loading Conditions

Mechanical Properties and Damage Failure of Carbon Fiber Reinforced Polymer Composite Sandwich Structure with Square Honeycomb Core Using the Interlocking Method

Tensile Mechanical Properties of Metal Honeycomb Sandwich Structure with Interface Connection Defects

Experimental and Numerical Investigation of Static and Fatigue Behaviors of Composites Honeycomb Sandwich Structure

Deformation behaviors of defective aluminum honeycomb sandwich panels subjected to in-panel compressive loading: an experimental study with mirror-assisted multi-view DIC

Mechanical responses of a composite sandwich structure with Nomex honeycomb core

Experimental and Numerical Studies on Defect Characteristics During Milling of Aluminum Honeycomb Core

Research on Filling Repair for Honeycomb Sandwich Structures

Local Strengthening Design and Compressive Behavior Study of the Triangular Honeycomb Structure

Bending Performance of Carbon Fiber–reinforced Polymers/aluminum Sandwich Structure with Different Forming Process and Analysis of Failure Mode

Investigations on the Mechanical Properties of Composite T-Joints with Defects under Bending Loading