Experimental Investigation on Ablation Characteristic of Silicone Rubber Insulator under Particle Erosion Condition
Yang LIU,Yi-wen GUAN,Yu-fei WU,Jiang LI,Jian CHEN,Min WANG
DOI: https://doi.org/10.13675/j.cnki.tjjs.2017.01.030
2017-01-01
Abstract:Focused on the ablation characteristics of silicone rubber enhanced by chopped carbon and high silica glass fiber under high temperature and concentration particle erosion condition,thirteen hot firing ablation experiments which range of particle concentration, erosion velocity and angles are 34.5~75.3kg/m3, 9.4~35.9m/s,19.3°~55.5°,respectively,have been performed on test motor. The ablation rates of silicone rubber insulator have been obtained under different particle erosion condition. Based on the results of ablation rate and character of the insulator, the ablation mechanism of silicone rubber insulator under particle erosion condition has been discussed. The results show that: (1) compared with the EPDM ablation results,the char layer of the silicone rubber insulator is more dense and thick than EPDM’s,and the maximum ablation rates of the silicone rubber insulator are sensitive with the change of the particle concentration. When particle concentration is beyond 50kg/m3 of the particle concentration,the ablation rate increases sharply. And with increasing of particle erosionvelocity, the ablation rate of silicon rubber insulator increases acutely at first and then increases slowly. (2) Under low particle erosion velocity condition,the ablation rates of EPDM were lower than silicon rubber’s,but under high particle erosion velocity condition, the ablation rates of EPDM were higher than silicon rubber’s. (3) The pyrolysis interval of silicone rubber is about 623~989K. During the ablation process,SiO2 produced by pyrolysis of high silica glass fiber and silicon rubber will permeate into the porous of char layer , and will react with the C in char layer to form the SiC. Then the char layer is densified and can endure particle erosion. (4) Through the morphology observation and analysis, the ablation physics model of silicon rubber insulator with three-layer and one-surface ablation structure (original layer, pyrolysis layer, char layer, particle erosion surface) is put forward.