Direct Preparation of LiBH4 from Pre-Treated LiH + B Mixture at High Pressure

Rugan Chen,Xinhua Wang,Lou Xu,Hui Li,Changpin Chen,Lixin Chen,Hongge Pan

DOI: https://doi.org/10.1016/j.jallcom.2010.09.215

2011-01-01

ChemInform

Abstract:LiBH4 was prepared from LiH+B mixture at 300–500°C with a hydrogen pressure of 35MPa. The LiH+B mixture was pretreated by ball milling under 10MPa hydrogen pressure for 10h. The results showed that ball-milling treatment is favorable for the formation of LiBH4, which could reduce the reaction temperature for about 200°C. A small quantity of LiBH4 could be found in the pre-treated sample. The formation of LiBH4 from LiH+B mixture is a kinetically hindered progress and a diffusion-control reaction. LiBH4 formed at 400°C could release 6.59wt.% H2 when it was heated from room temperature to 500°C. The yield of LiBH4 is about 59.4%.