Abstract:Herein, anodic aluminum foils are prepared using the dual‐phase enabled sinusoidal current anodizing method, which utilizes the sinusoidal nature of AC current to increase crystallinity in the high‐current‐density phase and to reduce defects in the low‐current‐density phase, increasing the specific capacitance of the foils by 23% and decreasing the time consumed by 60%. The anodized aluminum oxide prepared by anodizing is the core of aluminum electrolytic capacitors, and its quality determines the performance of aluminum electrolytic capacitors. The traditional direct current (t‐DC) anodizing method commonly used in industrial production today with low current density has the problems of low anodizing efficiency, poor crystallinity, and high formation constants of the oxide film. However, high current density direct current anodizing has the problems of severe defects of the oxide film and much thermal dissolution of aluminum foil. Herein, the dual‐phase enabled sinusoidal current (DESC) anodizing method is proposed for the preparation of 200 V anodized aluminum foil with much higher efficiency and performance. After testing, it is found that the alumina prepared by the DESC method has higher crystallinity and fewer defects. Consequently, the specific capacitance of the DESC sample is 23% greater than that of the t‐DC anodized sample, while the former displays a lower loss angle tangent and leakage current. Meanwhile, DESC anodizing takes 60% time less than t‐DC anodizing due to its high current density. The DESC anodizing method has been identified as a promising avenue for further investigation, exhibiting high efficiency and performance.

Research on the Anodic Aluminum Oxide As Anodic Foil of Aluminum Electrolytic Capacitor

Fabrication and Characterization of the Hierarchical AAO Film and AAO-MnO2 Composite As the Anode Foil of Aluminum Electrolytic Capacitor

Symmetric Pulsed Anodizing of Aluminum Foil for Aluminum Electrolytic Capacitors

Preparation of High Dielectric Constant Composite Oxide Films for Aluminum Electrolytic Capacitors

Research Development of Preparation Technology of High Voltage Anode Aluminum Foil

Preparation of Al2O3/TiO2 Composite Film with High Specific Capacitance by Surface Self-assembly Method

Improvement upon anode oxide film on etched aluminum foil for electrolytic capacitor

Progress in preparing anode aluminum foils of high specific capacitance for electrolytic capacitors

Comparative Research on Etched Aluminum Foils Fabricated by Different Techniques for Aluminum Electrolytic Capacitor

Surface Modification of Al Foils for Aluminum Electrolytic Capacitor

Formation and Property of Al2O3-TiO2 Composite Anodic Oxide Film on DC-Etched Al Foil for Al Electrolytic Capacitors

Preparation of Nb2O5-Al2O3 Composite Anodic Oxide Film for an Aluminum Electrolytic Capacitor by Electrodeposition-Annealing and Anodization

On the etching mechanism of surface area enlarging of aluminum foils used as high-voltage electrolytic capacitors anodes

Research Progress of Valve Metal Compound in High Specific Capacitance Aluminum Electrolytic Capacitors

Formation of Al2O3–Nb2O5 Composite Oxide Films on Low-Voltage Etched Aluminum Foil by Complexation–precipitation and Anodizing

Progress in the Studies of Anode Foils for High Voltage Electrolytic Capacitor

Anodizing model and CV simulation for etched aluminium foil for high voltage

Dual‐Phase Enabled Sinusoidal Current Anodizing for Efficient Preparation of High Specific Capacitance Anode Aluminum Foils

Study on Mechanism of Electrochemical Corrosion of Al-foil for Aluminum Electrolytic Capacitor Anode

Effect of azelaic acid on microstructure evolution and electrical properties of anodic aluminum foil for electrolytic capacitor

Voltage oscillations during anodizing process of aluminum and their suppression