Study of PA-TOFD Inspection based on Numerical Simulation
Shuxiao ZHANG,Lili LIU,Donghui ZHANG,Huimin YANG,Yunlong FANG,Da KANG,Shijie JIN,Kan ZHANG,Zhongbing LUO,Li LIN
2016-01-01
Abstract:Time of flight diffraction (TOFD) technique and phased array ultrasonic testing (PAUT) have been developed rapidly in the last decades. They have shown the tendency to replace traditional volumetric weld inspection techniques, such as radiography and pulse-echo ultrasonic testing. The TOFD inspection with s ector can phased array not only retained the high positioning accuracy of TOFD technique, but also obtained higher detection sensitivity over the entire range of test piece thickness . In this paper, the model of a 48.0mm thick carbon steel weld was establis hed, n which the depth of defects was from 2.0mm to 46.0mm and the heigh t was from 1.0mm to 3.0mm. The TOFD technique combined with sector scan phased arra y method, i.e. PA-TOFD, was simulated based on the model with CIVA softwar e. A series of TOFD D scanning images under different sector scanning angles wer obtained and analyzed in one run. The echo amplitude and the positioning ac curacy of defects measured by PA-TOFD method were compared with that of conventio al TOFD technique respectively. Result shows that the PA-TOFD method can accurately determine the depth of defects by extracting the defect signals at favor ble angle, and the defects with different depths can achieve higher echo amplitude. This method has the advantages of phased array technique, such as beam steer ing, energy focusing, as well as the high positioning accuracy of TOFD technique. I t is significant for improving the reliability and efficiency of weld detection.