Abstract:Silicon carbide (SiC) nanowires coexisting with amorphous graphite particles were initially produced by using silicon powder, tetrachlorethylene, metallic Na, and sulfur powder as reactants in an autoclave at 130 degrees C. Pure beta-SiC could be finally obtained after heating the sample in concentrated H2SO4 by refluxing at 180 degrees C, which was proved by the X-ray powder diffraction patterns. Transmission electron microscopy (TEM) images and scanning electron microscope (SEM) images show that the product is mainly composed of SiC nanowires (over 75 %) with an average diameter of about of 30 run and lengths up to tens of micrometers. High-resolution TEM shows that the nanowires have preferential growth along the [111] direction. It was found that when sulfur was absent, crystalline beta-SiC powders could not be obtained unless the target temperature was raised higher than 270 degrees C. In the mean time, the ratio of the nanowires also dropped dramatically (approximate to 20 %). The effects of sulfur, reaction time, and temperature on the morphologies of the final products, together with the properties of the final products, were also discussed. ((C) Wiley-VCH Verlag GmbH & Co. KGaA, 69451 Weinheim, Germany, 2008).

Synthesis of SiC Nanowires with Silica Sol and Carbon Black

Several Millimeters Long SiC–SiOx Nanowires Synthesized by Carbon Black and Silica Sol

Theoretical and experimental study of the mechanism for preparation of SiC nanowires by carbothermal reduction

Preparation of Silicon Carbide Nanowires by Carbothermic Reduction

Synthesis of SiO2 covered SiC nanowires with milled Si,C nanopowders

In-situ synthesis of SiC nanowires on biomass carbon materials derived from cherry stones

Synthesis and Characterization of SiC Nanowires Using Silicon Evaporation

Synthesis and Characterization of SiC Nanowires Using Carbon-Thermal Reduction

Direct synthesis of SiC nanowires by multiple reaction VS growth

Synthesis of nanocrystalline silicon carbide powders

Formation of silicon carbide nanotubes and nanowires via reaction of silicon (from disproportionation of silicon monoxide) with carbon nanotubes.

Synthesis and Growth Mechanism of NbC–SiC Micro/nanowire by Carbothermal Reduction

Rapid, Low-Temperature Synthesis Of Beta-Sic Nanowires From Si And Graphite

Synthesis of β-SiC nanowires by ball milled nanoparticles of silicon and carbon

Synthesis of Silicon Carbide Nanowires in a Catalyst-Assisted Process

Synthesis and Photoluminescence Property of Silicon Carbide Nanowires Via Carbothermic Reduction of Silica.

Sulfur‐Assisted Approach for the Low‐Temperature Synthesis of Β‐sic Nanowires

Nanocarbon-dependent synthesis of one-dimensional bead-chain-like β-SiC

Synthesis and Characterization of SiC Nanowires Through a Reduction−Carburization Route

Large-scale synthesis and characterization of hexagonal prism-shaped SiC nanowires.

Preparation of SiC Nanowires on Graphite Paper with Silicon Powder