Abstract:The object of this study is to investigate the structure of cast magnesium alloy (Mg-Al-Zn) inoculated with nano particles of different allotropic forms of carbon. The aim of this study is to improve the processability and quality of critical load bearing magnesium alloy part castings. The tasks of the study are: attainment of efficient control of the alloy structural features by introduction of incremental additions of carbon nano particles; determination of the relationship between the quantity of the added inoculating carbon agent and α - solid solution grain size; determination of the influence of allotropic forms of carbon on the morphologic characteristics of the intergranular borders and the eutectoid (a+Mg17Al12); and comparative analysis of the phase composition of the standard ML5 alloy and the experimental alloy ML5 inoculated with carbon black, nanographite, and single-wall carbon nanotubes. The phase composition was determined by X-ray diffraction analysis using copper radiation. Micro X-ray spectral analysis was performed. The following findings were obtained. Using an optical microscope α – solid solution grain size was measured in the standard and inoculated alloy. In the samples of the alloy variants inoculated with 0.1 % wt. of carbon black, nanographite, and single-wall carbon nanotubes, the grain size was reduced by appox. 50 % compared with the standard alloy. In the samples of the alloy inoculated with 0.1 % wt. of nanographite and single wall carbon nanotubes, eutectoid (a+Mg17Al12) precipitates along the grain boundaries were thinner than those in the standard alloy samples and those inoculated with carbon black. X-ray diffraction analysis revealed no new phase formation. The X-ray diffraction patterns of the alloy samples with nanographite and nanotubes display weak peaks of free carbon, which may indicate the presence of free carbon in small quantities in the structure. The scientific and practical originality of the obtained results consists of the following: a technology of inoculation with incremental additions of allotropic forms of nano carbon, namely carbon black, nanographite, and single-wall carbon nanotubes, has been tested on a standard cast magnesium alloy (Mg-Al-Zn system) in an environment similar to the industrial production of critical magnesium cast components. It has been shown that the introduction of nanocarbon in a quantity of 0.1 % wt. can have a beneficial effect on the structural characteristics of ML5 cast magnesium alloy with no change in its phase composition. Nanographite and single wall carbon nanotubes with a regular structure contribute to the formation of thinner intergranular boundaries than amorphous carbon black.

Influence of Fe on the Formation of Nucleation in Carbon-Inoculated Mg-3%Al Alloy

Effects of Mn Addition and Addition Sequence on Carbon Inoculation of Mg-3%Al Alloy

Effect of Mg on Nucleation Process of Recrystallization in Al–Mg–Si/SiCp Composite

Evolutions of grain size and nucleating particles in carbon-inoculated Mg-3% Al alloy

Influence of Fe on grain nucleation and growth of pure aluminum during refining by Al-Ti-B and Al-Ti-C master alloys

A new heterogeneous nucleation mechanism of AM30 alloy refined by carbon inoculation

Influence of Co Contents and Super-Gravity Field on Refinement of In-Situ Ultra-Fined Fibers in Al-2.5Ni Eutectic Alloys

Evolution behavior of Fe and Fe-rich phases in high-Fe concentration Al-Si-Mg alloy with Mn, Cr, and Co alloyed

Effect of Al Content on Inclusions in Fe‐15Mn‐xAl‐C Low‐Density Steel

Influence of carbon nanoparticle inoculation on the structure of ML5 casting magnesium alloy

Mg adsorption on MgAl2O4 surfaces and the effect of additive Ca: A combined experimental and theoretical study

Effect of Fe on the formation of NiAl intermetallic light beam surfacing layer and its microstructure

Preparation of Al3Ti-Al2O3/Al Inoculant and Its Inoculation Effect on Al-Cu-Mn Alloy

Effect of ferrochromium (FeCr) and ferroniobium (FeNb) alloys on inclusion and precipitate characteristics in austenitic stainless steels

Effect of Al Content on the Agglomeration Behavior of Inclusions in High Al Steel

Study on the mechanism of AF nucleation induced by complex oxide inclusions after LF refining in oxide metallurgical steel

Effect of Mg–Ti Treatment on Nucleation Mechanism of TiN Inclusions and Ferrite

Grain Refinement of Superalloy In718c by the Addition of Inoculants

Grain Coarsening Behavior of Mg-Al Alloys with Mischmetal Addition

Influence of cerium treatment on inclusion modification and as-cast microstructure of high-strength low-alloy steel