Effect of Counterpart'S Surface Micromorphology on Tribological Behavior of Nylon under Dry Sliding Contact

Chuan Hui Huang,Ming Ding,Hua Zhu
DOI: https://doi.org/10.4028/www.scientific.net/amr.199-200.615
2011-01-01
Advanced Materials Research
Abstract:This paper investigated the friction and wear behaviors of nylon rubbing against steel discs with helical, parallel and multidirectional textures respectively. The results indicated that friction coefficient, friction temperature and wear rate of couple using helical texture steel disc as counterpart were higher than others. Abrasive wear was the primary mechanism of the three couples. Nylon surface roughness increased after rubbing against helical texture steel disc, but decreased after rubbing against parallel and multidirectional texture steel discs. The roughness of both helical and multidirectional texture steel discs increased slightly after test, while the roughness increase of parallel textual steel disc was significant only at regions perpendicular to the rotating direction due to adhesion of nylon transfer film.
What problem does this paper attempt to address?