Abstract:The 2195 Al-Cu-Li alloy is widely utilized in the aerospace industry due to its lightweight nature and high strength. Consequently, gaining a comprehensive understanding of techniques to enhance its microstructural and mechanical properties is crucial for the consistent production of reliable and high-strength aerospace components. In this investigation, a pristine 2195 industrial ingot was subject to three distinct forging pretreatments: PT1, which involved a direct three upsetting and three stretching (3U3S) process; PT2, which combined double stage homogenization (DH) with 3U3S; and PT3, which involved DH along with six upsetting and six stretching (6U6S). Subsequent warm deformation and T8 aging treatment were applied to the pretreated forgings. The microstructure evolution during the processes and the final mechanical properties in three orthogonal dimensions were examined. The findings revealed that the combination of DH and multi-dimensional forging (MDF) facilitated the dissolution of non-equilibrium phases to a greater extent. Consequently, the main strengthening phase transformed from the T 1 + δ` phase observed in PT1 to the denser T1 + little θ` phase observed in PT2 and PT3 after T8 aging treatment. Notably, the tensile strength and yield strength of PT2 and PT3 specimens increased by 20-30 MPa in all three directions. Moreover, the MDF process accelerated the recrystallization behavior from PT1 to PT3, resulting in a gradual reduction in the average grain size of the pretreated samples from 356 μm to 186 μm. Following warm forging and T8 aging, the grains exhibited a finer and equiaxed structure. Additionally, the coarse phase was identified as the primary source of transgranular cracking. The coarse phases within the matrix became more homogeneous and finer from PT1 to PT3, with a gradual decrease in their area fraction. On the fracture surfaces, the aggregation of coarse phases diminished. Consequently, the elongation in the z-direction improved, and the elongation anisotropy and standard deviation decreased in all three directions for PT3 specimens. The findings presented in this study provide valuable insights into the high-performance manufacturing of Al-Cu-Li alloys.

Fabrication of Ti-43Al-5V-4Nb intermetallic compounds by forging using the blended elemental powders

In-situ alloying of Ti-5Fe titanium alloy using direct powder forging and the effect of the powder mixing method

Mechanical and Physical Characterizations of a Three-Phase TiAl Alloy during Near Isothermal Forging

The Effect of the Forging Process on the Microstructure and Mechanical Properties of a New Low-Cost Ti-5Al-1.5Mo-1.8Fe Alloy

Fabrication of multi-functional Ni–Ti alloys by laser powder bed fusion

Behaviour of novel low-cost blended elemental Ti-5Fe-xAl alloys fabricated via powder metallurgy

Effects of multi-directional forging on the microstructure and mechanical properties of TiB2 particulate reinforced 6061Al composite

Effect of forging pretreatment on the microstructures and mechanical properties of the Al-Cu-Li alloy

Effect of Forging on Microstructure and Properties of Al-9Si-5Cu-0.2Zr-0.1Sr-0.16Ti-0.1Ce Cast Aluminum Alloy

Microstructures and mechanical properties during sinter-forging of a novel TiAl alloy

Fabrication of Integrated Ni-Ti Alloys Possessing Both Super-elastic and Shape Memory Properties by Laser Powder Bed Fusion

Improvement on high-temperature tensile strength and ductility of selective electron beam melting TiAl alloys via small-strain forging

Additive manufacturing of titanium alloys with enhanced strength and uniform ductility via multi-element alloying

Crystallographic orientation and slip behavior of powder metallurgy Ti–6Al–4V via multi-directional forging

Micro-mechanism and mechanical properties of solid-powder hot isostatic pressing diffusion-bonded Ti2AlNb alloy

High Nb–TiAl Intermetallic Blades Fabricated by Isothermal Die Forging Process at Low Temperature

Mechanical alloying and direct powder forging of Ni–20Cr–20Fe-0.08C alloy

Influence of Forging Temperature on the Microstructures and Mechanical Properties of a Multi-Directionally Forged Al–Cu–Li Alloy

Fabrication of Ti3Al-Based Intermetallic Alloy by Laser Powder Bed Fusion Using a Powder Mixture

Refinement mechanism of centimeter-grade coarse grains in as-cast Ti 2 AlNb-based alloy during multi-directional forging

Achieving high strength-ductility synergy in a hierarchical structured metastable β-titanium alloy using through-transus forging