Four-point bending test of high-early-strength high ductility concrete (HES-HDC): early mechanical behavior and toughness evaluation
Jiasheng Yang,Mingke Deng,Yangxi Zhang,Hongkan Fan,Yang, Jiasheng,Deng, Mingke,Fan, Hongkan
DOI: https://doi.org/10.1007/s43452-023-00847-9
IF: 4.042
2024-01-16
Archives of Civil and Mechanical Engineering
Abstract:To investigate the early mechanical response of high-early-strength high ductility concrete (HES-HDC), a four-point bending test was conducted. The effects of fiber type, fiber content, curing age, sand-binder ratio ( s / b ), and hydroxypropyl methylcellulose (HPMC) content on the crack pattern, load–deflection curve, flexural strength, and deflection of HES-HDC were studied. Based on the test results, a flexural toughness evaluation method suitable for the characteristics of HDC was proposed. The results showed that under flexural load, the load–deflection curve of HES-HDC exhibited a deflection-hardening response, with multiple cracks developed during the failure process. The flexural strength of HES-HDC reaches more than 5 MPa in 2 h, meeting the requirements for open traffic. Fiber type, fiber content, and curing age had a significant impact on the cracking behavior, deflection-hardening response, and flexural strength of HES-HDC. The higher the fiber pullout proportion and bridging stress during the crack-bridging was, the higher the deflection and energy absorption of HES-HDC exhibited. The existing flexural toughness evaluation methods were not applicable for HDC assessment due to their inability to consider the influence of different fiber types on the deflection-hardening response of HDC. A flexural toughness index in the form of energy ratio and a flexural strength coefficient in the form of strength ratio was proposed, which can effectively evaluate the flexural toughness of the HES-HDC beam during its whole loading process. This method took into account the large deformation of HDC and eliminated the influence of specimen size by using dimensionless forms.
engineering, mechanical,materials science, multidisciplinary, civil