Abstract:The possible fracture process of interior texture and its reinforcing mechanism to properties. Polyacrylonitrile (PAN)‐based precursor fibers with different mechanical properties prepared by wet‐spinning and its correlation with microstructure was researched, the primary structural factors that affecting its properties were analyzed. The tensile strength and modulus of precursor fibers increased from 4.63 cN/dtex to 9.16 cN/dtex and 99.09 cN/dtex to 168.92 cN/dtex, respectively, with the increase in crystallinity from 69.29% to 87.84% and orientation degree increased from 83.95% to 93.81%, high performance precursor fibers could be achieved by decrease in the crystallite size and interlayer spacing, these aggregation structure plays a decisive role to the mechanical properties of fibers. The integrality of aggregation structure and properties could reflected by boiling water shrinkage behavior and glass transition temperature from the side. The fracture morphology of fibers with different properties were studied by scanning electron microscope (SEM) and three fracture characteristics were observed, PF1 and PF3 presented the radial extended fracture without microfibril pull out, radial cluster fracture with the pull out of microfibril for PF2, PF4–PF6, together with the axial splitting pattern in PF6, which was revealed by microfibrils/fibrils in longitudinal and transverse combined with solution etching. Precursor fibers with less voids, without serious skin‐core, continuous arrangement, tightly stacked, well‐developed and complete oriented microfibrils/fibrils, exhibited excellent mechanical properties. Possible fracture process was given from the perspective of aggregation structure and microfibrils/fibrils, which become dominant factors determining properties of precursor fibers. Improve the performance could be achieved by regulating surface structure and cross‐sectional shape. As one of the main structural factors that determining properties, by reducing diameter could minimize the numbers and sizes of defects.

Effect of Solvent Residuals on the Structure and Properties of Polyacrylonitrile Fibers

Study on the structural evolution of polyacrylonitrile fibers in stepwise heat treatment process and its relationship with properties

Effect of the Casting Solvent on the Crystal Characteristics and Pervaporative Separation Performances of P(Vdf-Co-Hfp) Membranes

Effect of Coagulation Conditions on the Radial Moduli of Polyacrylonitrile Nascent Fibers

Electrospun Nanofibers Withstandable to High-Temperature Reactions: Synergistic Effect of Polymer Relaxation and Solvent Removal

Study on the Changes of Structures and Properties of PAN Fibers during the Cyclic Reaction in Supercritical Carbon Dioxide

INFLUENCE OF THERMAL TREATMENT ON CRYSTAL MELTING BEHAVIOR AND CRYSTAL STRUCTURE OF NYLON 6 AND POLYAMIDE BLOCK COPOLYMER/NYLON 6 BLENDS

Comprehensive research on the correlation between microstructure and mechanical properties of polyacrylonitrile‐based precursor fibers prepared by wet‐spinning

Effects Of Water Solubility Of Acrylonitrile On Vinylidene Chloride/Acrylonitrile/Styrene Suspension Polymerization

Effects of Moisture Content and Heat Treatment on the Viscoelasticity and Gelation of Polyacrylonitrile/Dimethylsulfoxide Solutions

Microstructural Evolution during Dry-Jet Wet Spinning Postprocessing from Coagulation Bath Fiber to High-Performance Polyacrylonitrile Precursor Fiber

Effect of Coagulation Bath Concentration on the Structure and Properties of Polyacrylonitrile As-Spun Fibers During Wet-Spinning

Effect of amorphous carbon on the tensile behavior of polyacrylonitrile (PAN)-based carbon fibers

Effects of Solvent on Structures and Properties of Electrospun Poly(ethylene Oxide) Nanofibers

Effect of Jet Stretch on Polyacrylonitrile As‐spun Fiber Formation

Stabilization of polyacrylonitrile nanofiber mats obtained by needleless electrospinning using dimethyl sulfoxide as solvent

Effects of KBrO3 on Chemical, Aggregation and Morphological Structure of Polyacrylonitrile (PAN) Precursor Fibers

Interactions Between Polyacrylonitrile and Solvents: Density Functional Theory Study and Two-Dimensional Infrared Correlation Analysis.

Transformation of Specific Dispersion Interactions between Cellulose and Polyacrylonitrile in Solutions into Covalent Interactions in Fibers

Effect of the Ionic Liquid Structure on the Melt Processability of Polyacrylonitrile Fibers.

Structural Transformation of Polyacrylonitrile (PAN) Fibers during Rapid Thermal Pretreatment in Nitrogen Atmosphere