Abstract:The proton exchange membrane (PEM) is a critical portion of a proton exchange membrane fuel cell (PEMFC). However, it is strongly influenced by pinhole defects owing to degradation during its operation or manufacture. Such defects may accelerate chemical polymer decomposition, eventually causing fuel cell failure and other safety issues. Thus, it is necessary to detect and characterize pinhole degradation while determining the effect of pinhole on electrochemical behavior and fuel cell performance. Herein, pinholes of different sizes (10 and 100 μm) were fabricated on a 50-cm 2 catalyst-coated membrane (CCM) and characterized using commercial current scan shunt (CSS) S++ Simulation Services (Hephas Energy) to investigate the effects of pinhole size on current density and temperature distributions of the PEMFC. Our analyses show that hydrogen crossover from the anode to the cathode through a pinhole can cause hydrogen diffusion and a hydrogen oxidation reaction (HOR) on the cathode electrode surface under certain conditions. Consequently, local reverse currents and hot spots are detected around the pinhole position under open-circuit voltage (OCV) and the corresponding current and temperature distribution trends are uniform. Conversely, the reverse current immediately disappeared from the current distribution map because water exists under operation conditions, resulting in membrane swelling and pinhole sealing. Thus, hydrogen crossover decreased and local reverse currents reappeared as a result of anode overpressure during fuel cell operation. The local reverse current becomes weaker when using the same-sized pinhole under the same anode overpressure because the overall current density increases. Furthermore, owing to the presence of water, the capillary force for the 100-μm pinhole was higher than that for the 10-μm pinhole, indicating that more anode overpressure is required to generate a local reverse current. Thus, the position and size of the pinhole can be effectively detected using in situ characterization.

The Effects Of Pinholes On Proton Exchange Membrane Fuel Cell Performance

The pinhole effect on proton exchange membrane fuel cell (PEMFC) current density distribution and temperature distribution

Effect of pinholes in electrolyte on re‐oxidation tolerance of anode‐supported solid oxide fuel cells

Investigation of pinhole defects in gas diffusion layers for the quality control of proton exchange membrane fuel cells

Effects of Cracks on the Mass Transfer of Polymer Electrolyte Membrane Fuel Cell with High Performance Membrane Electrode Assembly

Research on the Long-Term Stability of a PEMFC Stack: Analysis of Pinhole Evolution

Mechanical degradation of proton exchange membrane along the MEA frame in proton exchange membrane fuel cells

Effects of Carbon Corrosion on Mass Transfer Losses in Proton Exchange Membrane Fuel Cells

Endplate effect in an open-cathode proton exchange membrane fuel cell stack: Phenomenon and resolution

Sealing Performance of Ethylene Propylene Diene Monomer Seals for Proton Exchange Membrane Fuel Cells

Degradation Study of Membrane Electrode Assembly with PTFE/Nafion Composite Membrane Utilizing Accelerated Stress Technique

Diagnosis of Membrane Electrode Assembly Degradation with Drive Cycle Test Technique

Influence of crack formation at the catalyst layer and membrane interface on the performance of PEMFC

Study on Assembly Error Effect on the Performance of Proton Exchange Membrane Fuel Cell Considering Membrane Electrode Assembly Deformation

A systematic investigation on the effects of Cu 2+ contamination on the performances and durability of proton exchange membrane fuel cells

Mechanical Degradation of Proton Exchange Membrane During Assembly and Running Processes in Proton Exchange Membrane Fuel Cells with Metallic Bipolar Plates

Mechanical Failure and Mitigation Strategies for the Membrane in a Proton Exchange Membrane Fuel Cell

Effect of flow channel shapes of proton exchange membrane fuel Cell on its performances

Effect of Micro-Cracks on the In-Plane Electronic Conductivity of Proton Exchange Membrane Fuel Cell Catalyst Layers Based on Lattice Boltzmann Method

Effect of load-cycling amplitude on performance degradation for proton exchange membrane fuel cell

Pore-scale and Multiscale Study of Effects of Pt Degradation on Reactive Transport Processes in Proton Exchange Membrane Fuel Cells