Scalable Polymeric Few-Nanometer Organosilica Membranes with Hydrothermal Stability for Selective Hydrogen Separation
Lingxiang Zhu,Liang Huang,Surendar R. Venna,Adrienne K. Blevins,Yifu Ding,David P. Hopkinson,Mark T. Swihart,Haiqing Lin
DOI: https://doi.org/10.1021/acsnano.1c03492
IF: 17.1
2021-07-13
ACS Nano
Abstract:Nanoporous silica membranes exhibit excellent H<sub>2</sub>/CO<sub>2</sub> separation properties for sustainable H<sub>2</sub> production and CO<sub>2</sub> capture but are prepared via complicated thermal processes above 400 °C, which prevent their scalable production at a low cost. Here, we demonstrate the rapid fabrication (within 2 min) of ultrathin silica-like membranes (∼3 nm) via an oxygen plasma treatment of polydimethylsiloxane-based thin-film composite membranes at 20 °C. The resulting organosilica membranes unexpectedly exhibit H<sub>2</sub> permeance of 280–930 GPU (1 GPU = 3.347 × 10<sup>–10</sup> mol m<sup>–2</sup> s<sup>–1</sup> Pa<sup>–1</sup>) and H<sub>2</sub>/CO<sub>2</sub> selectivity of 93–32 at 200 °C, far surpassing state-of-the-art membranes and Robeson's upper bound for H<sub>2</sub>/CO<sub>2</sub> separation. When challenged with a 3 d simulated syngas test containing water vapor at 200 °C and a 340 d stability test, the membrane shows durable separation performance and excellent hydrothermal stability. The robust H<sub>2</sub>/CO<sub>2</sub> separation properties coupled with excellent scalability demonstrate the great potential of these organosilica membranes for economic H<sub>2</sub> production with minimal carbon emissions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c03492?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c03492</a>.Characterizations (SEM, XPS, AFM, Raman, FT-IR, XRD, and water contact angle) of porous PBI support, PDMS coating, and POSi membranes; activation energy determination for H<sub>2</sub> and CO<sub>2</sub> permeation across a POSi120 membrane, separation performance of a POSi120 membrane after being aged for 340 d, and schematic illustrations of the plasma treatment equipment and gas permeation apparatus. XPS deconvolution results, XPS depth profiling results, gas permeance of PDMS membranes, and detailed H<sub>2</sub>/CO<sub>2</sub> separation properties and testing conditions of the membrane materials selected for comparison in <a class="internalNav" href="#fig4">Figure </a><a class="internalNav" href="#fig4">4</a> (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c03492/suppl_file/nn1c03492_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology