Preparation and corrosion resistance of composite coatings on magnesium alloy

SHANG Wei,CHEN Bai-zhen,SHI Xi-chang,WEN Yu-qing,HUANG An-sheng
2011-01-01
Abstract:Composite coatings consisted of a MAO layer and a sol-gel layer were obtained on a magnesium alloy by micro-arc oxidation (MAO) and sol-gel technique. The surface morphologies and composition of the MAO coating and the composite coatings were analyzed by scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS). Potentiodynamic polarization curves were used to investigate the electrochemical properties of the composite coatings formed under different conditions. The results show that the optimum conditions are obtained as follows. Coated frequency is 3 times, soak time is 1 min, drying temperature is controlled within 80-100°C, drying time is 8 h, curing temperature and curing time are 170°C and 1 h, respectively. SiO 2 sol-gel film could effectively seal micropores in the MAO coating. The composite coatings are more uniform and compact than the MAO coating. The polarization result shows that the composite coatings have more positive corrosion potential (E corr), lower corrosion current density (i corr), and higher linear polarization resistance (R p) than the MAO coating and magnesium alloy substrate, indicating that the sol-gel coating formed on the magnesium alloy with MAO coating under the optimum conditions has better corrosion resistance. The composite coatings have good protection to magnesium alloy AZ91D.
What problem does this paper attempt to address?