Abstract:In this work, Mg–7Y–5Zn-0.1V alloys were prepared by 1-D forging followed by multi-step rolling. The rolling reduction dependence of the microstructure and tensile properties of the Mg–7Y–5Zn-0.1V alloy was experimentally investigated. The results indicated that the bimodal matrix microstructures are formed, and the fibrous 18R long-period stacking ordered (LPSO) phase and kinked 14H-LPSO phase are observed after 1-D forging. As the rolling deformation increased, the fibrous 18R-LPSO fractured into block and distributed more homogeneous. The lamellar 14H-LPSO fractured more severely, and it re-precipitated within the matrix when the deformation reached 50 %. The average grain size decreased gradually with increasing rolling deformation, and the minimum was 5.07 μm. After rolling, the {0001} <11 2 ̅ 0> and {0001} <10 1 ̅ 0> textures disappeared. The grain refinement of rolling alloy was mainly due to the fact that dynamic recrystallization (DRX) and substructures were generated within some grains, while the forging alloy was mainly due to DRX. The mechanisms of DRX were discontinuous DRX (DDRX) and twin-induced DRX (TDRX) after forging, and continuous DRX (CDRX) and DDRX after rolling. The strength reached its maximum when the rolling deformation amount reached 60 %, with a yield strength (YS) of 350 MPa and an ultimate tensile strength (UTS) of 385 MPa. Compared to the as-cast Mg–7Y–5Zn-0.1V alloy, its strength increased by 56 % and 63 %, respectively. The improvement of mechanical properties was mainly attributed to fine grain strengthening and dislocation strengthening.

Microstructure refining and property improvement of ZK60 magnesium alloy by hot rolling

Evolution of Microstructure and Mechanical Properties of ZK60 Magnesium Alloy Processed by Asymmetric Lowered-Temperature Rolling

Microstructure and Mechanical Properties of Thin ZK61 Magnesium Alloy Sheets by Extrusion and Multi–pass Rolling with Lowered Temperature

Optimization of Rolling Condition for ZK61 Alloy Sheets via Microstructure and Mechanical Property Analysis

Fabrication of ZK60 Magnesium Alloy Thin Sheets with Improved Ductility by Cold Rolling and Annealing Treatment

Property Improvements in Fine–grained Mg–Zn–Zr Alloy Sheets Produced by Temperature–step–down Multi–pass Rolling

Microstructure Evolution and Mechanical Performance Improvement of Thin ZK61 Magnesium Alloy Sheets Subjected to Cumulative Cold Rolling and Intermediate Annealing

Effect of Hot Rolling on Grain Refining and Mechanical Properties of AZ40 Magnesium Alloy

Evolution of Microstructure, Texture and Mechanical Properties of ZK60 Magnesium Alloy in a Single Rolling Pass

Plastic Deformation Mechanism of High Strength and Toughness ZK61 Magnesium Alloy Plate by Multipass Horizontal Continuous Rolling

Homogeneity improvement of friction stir welded ZK61 alloy sheets in microstructure and mechanical properties by multi-pass lowered-temperature rolling

Optimization of rolling temperature for ZK61 alloy sheets via microstructure uniformity analysis

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Microstructure and Mechanical Properties of Hot-Rolled Mg-Zn-Y-Zr Magnesium Alloy

The Dynamic Recrystallization and Mechanical Property Responses During Hot Screw Rolling on Pre-Aged ZM61 Magnesium Alloys

Microstructure and Mechanical Properties of Rolled Mg-12gd-3y-0.4zr Alloy Sheets

Microstructure and mechanical property of multi-pass low-strain rolled Mg-Al-Zn-Mn alloy sheet

Investigation of microstructure and mechanical properties of ZK60 magnesium alloy achieved by extrusion-shearing process

Effect of Deformation Temperature on Texture and Mechanical Properties of ZK60 Magnesium Alloy Sheet Rolled by Multi-Pass Lowered-Temperature Rolling

Effect of Rolling Deformation on Microstructure and Mechanical Properties of As-Cast and Rolled ZM21 Magnesium Alloy

Achieving enhanced mechanical properties in the Mg–Y–Zn–V alloy by refining grains and improving the morphology and distribution of LPSO via pre-forging and subsequent rolling