Abstract:Magnesium (Mg) sheets that are thinner than 1 mm show significant advantages in the fabrication of shells of electronic equipment, as they are lightweight while also providing excellent electromagnetic shielding. Rolling is the most commonly used method for preparing such thin sheets, but it easily leads to edge cracks and poor mechanical properties related to the evolution of grain structure and texture. To this end, a two-stage rolling process under decreasing temperature conditions is proposed to obtain thin Mg alloy sheets with satisfied surface quality and excellent mechanical properties. The results demonstrated that after two-stage rolling, the thin sheets show satisfied surface quality, basically without edge cracks. The grain structure of the Mg sheets with thicknesses of 1.0, 0.6, 0.3, and 0.1 mm is homogeneous and significantly refined, with the smallest average grain size being approximately 5.3 μm. The 1.0-mm thin sheet exhibits a bimodal texture that transforms into a conventional (0001) basal texture as the rolling process proceeds. This is due to the low deformation temperature during warm rolling, which makes it difficult to activate non-basal slip, and thus, basal slip dominates deformation. Furthermore, based on the effect of inhomogeneous texture components and different Schmid factors in varying directions, all thin sheets show anisotropy in mechanical properties. The 0.6-mm thin sheet indicates a good combination of superior strength and medium ductility, which can be attributed to the combined effect of grain refinement and dislocation strengthening.

Microstructure and Mechanical Properties of Thin ZK61 Magnesium Alloy Sheets by Extrusion and Multi–pass Rolling with Lowered Temperature

Evolution of Microstructure and Mechanical Properties of ZK60 Magnesium Alloy Processed by Asymmetric Lowered-Temperature Rolling

Microstructure Evolution and Mechanical Performance Improvement of Thin ZK61 Magnesium Alloy Sheets Subjected to Cumulative Cold Rolling and Intermediate Annealing

Optimization of Rolling Condition for ZK61 Alloy Sheets via Microstructure and Mechanical Property Analysis

Fabrication of ZK60 Magnesium Alloy Thin Sheets with Improved Ductility by Cold Rolling and Annealing Treatment

Property Improvements in Fine–grained Mg–Zn–Zr Alloy Sheets Produced by Temperature–step–down Multi–pass Rolling

Microstructure refining and property improvement of ZK60 magnesium alloy by hot rolling

Effect of Deformation Temperature on Texture and Mechanical Properties of ZK60 Magnesium Alloy Sheet Rolled by Multi-Pass Lowered-Temperature Rolling

Evolution of Microstructure, Texture and Mechanical Properties of ZK60 Magnesium Alloy in a Single Rolling Pass

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Homogeneity improvement of friction stir welded ZK61 alloy sheets in microstructure and mechanical properties by multi-pass lowered-temperature rolling

Optimization of rolling temperature for ZK61 alloy sheets via microstructure uniformity analysis

Plastic Deformation Mechanism of High Strength and Toughness ZK61 Magnesium Alloy Plate by Multipass Horizontal Continuous Rolling

Weakened anisotropy of mechanical properties in rolled ZK60 magnesium alloy sheets with elevated deformation temperature

Microstructure and Mechanical Properties of Hot-Rolled Mg-Zn-Y-Zr Magnesium Alloy

Microstructure, Texture Evolution, and Mechanical Properties of Thin AZ31B Mg Alloy Sheets Prepared by Two-Stage Rolling

Microstructure and Mechanical Properties of Large ZK60 Magnesium Alloy Extruded Profiles

Mechanical anisotropy improvement in ultrafine-grained ZK61 magnesium alloy rods fabricated by cyclic extrusion and compression

Tensile Properties, Texture Evolutions and Deformation Anisotropy of As-Extruded Mg-6Zn-1Zr Magnesium Alloy at Room and Elevated Temperatures

Dynamic precipitation and enhanced mechanical properties of ZK60 magnesium alloy achieved by low temperature extrusion

Microstructure and Tensile Properties of Mg-3Al-1Zn Sheets Produced by Hot-Roller-cold-material Rolling