Preparation and upconversion property of TeO2:Er 3+/Yb3+ nanoparticles

Hui Hu,Yan Bai,Minwen Huang,Biyin Qin,Jie Liu,Wenjie Zheng

DOI: https://doi.org/10.1016/j.optmat.2011.08.025

IF: 3.754

2011-01-01

Optical Materials

Abstract:Different crystal structure of TeO2 nanoparticles were used as the host materials to prepare the Er3+/Yb3+ ions co-doped upconversion luminescent materials. The TeO2 nanoparticles mainly kept the original morphology and phase after having been co-doped the Er 3+/Yb3+ ions. All the as-prepared TeO2:Er 3+/Yb3+ nanoparticles showed the green emissions (525 nm, 545 nm) and red emission (667 nm) under 980 nm excitation. The green emissions at 525 nm, 545 nm and red emission at 667 nm were attributed to the 2H11/2 → 4I15/2, 4S3/2 → 4I15/2 and 4F9/2 → 4I15/2 transitions of the Er3+ ions, respectively. For the α-TeO2:Er 3+/Yb3+ (3/10 mol%) nanoparticles, three-photon process involved in the green (2H11/2 → 4I 15/2) emission, while two-photon process involved in the green ( 4S3/2→4I15/2) and red ( 4F9/2 → 4I15/2) emissions. For the β-TeO2:Er3+/Yb3+ (3/10 mol%) nanoparticles, two-photon process involved in the green (2H 11/2 → 4I15/2), green (4S 3/2 → 4I15/2) and red (4F 9/2 → 4I15/2) emissions. It suggested that the crystal structure of TeO2 nanoparticles had an effect on transition processes of the Er3+/Yb3+ ions. The emission intensities of the α-TeO2:Er3+/Yb3+ (3/10 mol%) nanoparticles and β-TeO2:Er3+/Yb3+ (3/10 mol%) nanoparticles were much stronger than those of the (α + β)-TeO2:Er3+/Yb3+ (3/10 mol%) nanoparticles. © 2011 Elsevier B.V. All rights reserved.