Abstract:We prepared two kinds of monodispersed polystyrene (PS) microspheres with different surface electrical properties from the polymerization of styrene in water using different initiators. The PS microspheres prepared with potassium persulfate (KPS) as the initiator (PS-a) have negative zeta potential in water, and those prepared with 2,2'-azobis(2-methylpropionamidine) dihydrochloride (AIBA) as the initiator (PS-c) have positive zeta potential in water. Next, PS-a and PS-c microspheres were respectively used as the templates to prepare hollow SiO2 microspheres through a sol-gel process of tetraethoxysilane (TEOS) in an ethanol/ammonia medium. Based on the analysis on the products by FTIR, SEM, TEM, TGA, and N-2 adsorption-desorption isotherms, it was found that the distribution of OH- in the system depended on the surface electrical property of the PS template microspheres, which would lead to different formation processes of the silica shell on the template microspheres. When the PS-a microspheres were used as the template, the OH- ions were repulsed from the negative surface of the PS-a template microspheres, due to the electrostatic repulsion interaction. Thus, the SiO2 nanoparticles with a size of several tens of nanometers were firstly formed by hydrolysis and condensation of TEOS in the medium, and then adsorbed and packed on the surface of PS-a template microspheres through the polar interaction, resulting in the formation of a raspberry-like silica shell with macropores. After the PS-a template microspheres etched by toluene, the raspberry-like hollow silica microspheres were obtained. However, when PS-c template microspheres were used as the template, the OH- ions were adsorbed on the positive surface of the template microspheres. Then, a smooth and dense silica layer was grown directly from the surface of the template microspheres through the hydrolysis and the condensation of TEOS catalyzed by the adsorbed OH- ions. After calcination at 600 degrees C for 8 h, hollow silica microspheres with a smooth and mesoporous silica shell were produced. This work indicates that the morphology of the hollow silica microspheres can be controlled through the surface electrical property of the template microspheres. This study may lead to more applications of hollow silica microspheres in the area of control-release materials, drug carriers, and absorbents.

Synthesis of Hierarchical Hollow Silica Microspheres Containing Surface Nanoparticles Employing the Quasi-Hard Template of Poly(4-vinylpyridine) Microspheres

Hollow mesoporous silica with a hierarchical shell from in situ synergistic soft-hard double templates.

Facile fabrication of hollow mesoporous silica microspheres with hierarchical shell structure via a sol–gel process

Facile Fabrication of Hollow Silica Nanospheres and Their Hierarchical Self-Assemblies As Drug Delivery Carriers Through a New Single-Micelle-template Approach

Synthesis of Hollow Mesoporous Silica Microspheres Through Surface Sol–gel Process on Polystyrene-Co-poly(4-vinylpyridine) Core–shell Microspheres

Preparation of Hierarchical Mesoporous Silica Nanoparticles Through a Single-Templating Approach

Preparation of hollow silica spheres with different mesostructures

Controllable synthesis of silica hollow spheres by vesicle templating of silicone surfactants

Anionic Surfactants Templating Route for Synthesizing Silica Hollow Spheres with Different Shell Porosity

Efficient Synthesis of Hollow Silica Microspheres Useful for Porous Silica Ceramics

Novel and feasible method for synthesis of monodispersed hollow silicon dioxide submicrospheres

One-Pot Preparation of Hollow Silica Spheres by Using Thermosensitive Poly(N-Isopropylacrylamide) As A Reversible Template

Synthesis of silica hollow spheres with hierarchical morphology

Influence of the Surface Electrical Property of Polymer Template Microspheres on the Morphology of Hollow Silica Microspheres

A facile and novel approach for preparing monodispersed hollow aluminosilica microspheres with thin shell structures

Hollow Mesoporous Silica Spheres Synthesized with Cationic and Anionic Mixed Surfactant As Templates

Preparation of Hollow Silica Microspheres Via Poly(N-Isopropylacrylamide)

Hierarchic Template Approach for Synthesis of Silica Nanocapsules with Tuned Shell Thickness

Facile Preparation of Hierarchical Mesoporous Silica Microspheres with Tunable Porous Structure and Particle Sizes

Synthesis of Silica Hollow Spheres with Diameter Around 50 Nm by Anionic Surfactant

One-Step Synthesis of Monodisperse and Hierarchically Mesostructured Silica Particles with a Thin Shell