Temperature-Dependent Triple Crystal Polymorphism of Poly(hexamethylene Terephthalate): Long-Range Ordered Mesophase Formation and Crystal Structure–Property Relationships
Jianfei Xia,Lingling Ni,Chang Zeng,Bao Wang,Rui Zhang,Chenxuan Sun,Jian Song,Junfeng Liu,Chengtao Yu,Ying Zheng,Pengju Pan
DOI: https://doi.org/10.1021/acs.macromol.4c01107
IF: 5.5
2024-01-01
Macromolecules
Abstract:Terephthalic polyesters are important engineering plastics and can crystallize into multiple crystal phases, including the mesophase in processing. However, the formation process and structural characteristics for the unique long-range ordered mesophase of terephthalic polyesters are still not well understood. Herein, we investigated the crystal polymorphism, crystallization kinetics, phase transition, and mechanical properties of a medium-chain terephthalic polyester, poly(hexamethylene terephthalate) (PHT). A new long-range ordered mesophase (named as the delta phase) is discovered for PHT during quiescent melt crystallization at a low crystallization temperature (T-c = 10-30 degrees C). However, the alpha and beta crystal phases are crystallized at a medium (40-80 degrees C) and high (90-130 degrees C) T-c, respectively. The mesomorphic delta phase has a long-range order with a layered structure and inclined chain packing, which shows faster chain relaxation and smaller lamellar thickness than the alpha and beta phases. The mesomorphic delta phase is metastable and converts into the stable beta phase upon heating or high-temperature annealing. Mechanical properties of PHT can be well tuned by crystal polymorphs. The mesomorphic delta phase of PHT has good transparency and ductility, while the alpha and beta phases possess a higher yield strength and modulus. This work provides an in-depth understanding of the mesophase formation and complex crystal polymorphism of terephthalic polyesters.