Thin-Film Crystallization of Poly(butylene Terephthalate) from the Anisotropic Amorphous State
Bo-Yuan Zheng,Jia-Hui Wu,Zi-Fan Yang,Li-Dong Zheng,Shuang Yang,Ren Bao,Alexander Stroeks,Er-Qiang Chen
DOI: https://doi.org/10.1021/acs.macromol.3c01313
IF: 5.5
2023-01-01
Macromolecules
Abstract:Crystallization of poly(butylene terephthalate) (PBT) thin films from the glassy state has been investigated. The thin films on the silicon substrate with a thickness of no more than 300 nm were prepared by spin-casting and were examined by grazing-incidence X-ray scattering and atomic force microscopy before and after isothermal annealing at various temperatures (T(a)s). It is found that the virgin spin-cast thin films are anisotropic amorphous, with the PBT chains preferentially lying down on the substrate. The phase structure and morphology of the annealed thin films are strongly T-a-dependent. At T(a)s below 80 degrees C, the thin films remain amorphous due to the restricted chain segment mobility imposed by the one-dimensional (1D) confinement of the thin film. For T-a of 80-180 degrees C, isothermal annealing results in dominantly smectic nodules with a size of around 10 nm, which can be sustained regardless of extending the annealing time. When T-a is in the range of 180-200 degrees C, lath-like PBT crystals of alpha-form, which are edge-on lamellae, are observed to coexist with the smectic nodules. Further increasing T-a allows the lath-like crystals to grow substantially. However, owing to the high nucleation density, the crystals are small, showing a lateral size of just several dozens of nanometers. It is interesting to note that the 1D confinement condition could largely arrest the transformation from smectic-to-crystal over a wide temperature range, letting the smectic nodules survive at T-a below 200 degrees C. We further explored the interplay of smectic and crystal phases. It is unveiled that when the well-formed nodules are taken as the initial state for crystallization, the nodules can rapidly turn into nearly square-shaped crystal particles above 200 degrees C, which serve as the element blocks for the subsequent crystal growth. The combination of these blocks makes the lath-like crystals extend their lengths. Accordingly, we conjecture that when the PBT thin films are crystallized from the glassy state, there may exist a pathway of "glass-to-smectic-to-crystal".