Preparation and Luminescence Properties of Gd2o3:Eu3+@Y2o3 Core-Shell Nanomaterials

Bai Haiying,Liu Guixia,Dong Xiangting,Wang Jinxian
2011-01-01
Acta Chimica Sinica
Abstract:Gd2O3:Eu3+@Y2O3 core-shell structural luminescence nanomaterials were prepared by homogeneous precipitation method. XRD patterns show that the sample calcined at 800 degrees C is cubic phase Gd2O3, and the crystal grows well, after coated with Y2O3, the diffraction peak position of Gd2O3 is not changed, while with the increase of the coating thickness, cubic phase Y2O3 diffraction peaks appear. In FTIR spectra, it is observed that Gd-O, Y-O stretching vibration absorption peaks increase with decreasing the coating thickness, this reason is that when the coating thickness is suitable, the dangling bonds on the particle surface are less, which results in Gd(Eu,Y)-O bonds increase. SEM images indicate that the samples before and after coated are all in sphere shape. XPS analysis further proves that the Y2O3 is coated on the surface of Gd2O3:Eu3+. Photoluminescence properties show that coating the Y2O3 host with different thickness on the surface of Gd2O3:Eu3+ nanoparticles, the Eu3+ characteristic red emission can be observed. And when the coating thickness is suitable, that is Gd2O3:Eu3+/Y2O3 ratio of R=4 : 1, the luminescence intensities of core-shell particles are higher than that of the Gd2O3:Eu3+ core nanocrystals, it is thought that the core-shell samples decrease the negative effects of nanoparticles on the luminescence properties.
What problem does this paper attempt to address?