Preparation and Properties of Ag @ SiO2 @ Y2O3 : RE3 + (RE＝Eu, Tb)Core-Shell Structural Luminescent Materials

Chen Yan,Liu Guixia,Luan Dan,Dong Xiangting,Wang Jinxian,Sun Ping

2012-01-01

Abstract:Ag@SiO 2@(Y, RE)(OH)CO 3·H 2O (RE=Eu, Tb) core-shell structural microspheres were prepared via a homogeneous precipitation method. After heat treatment at 700°C, the core-shell structural Ag@SiO 2@Y 2O 3:RE 3+(RE=Eu, Tb) luminescent particles were obtained. The XRD patterns showed that the Ag core was face-centred cubic structure with good crystallinity, the SiO 2 layer was amorphous, and Y 2O 3 layer was cubic phase. The FTIR spectra showed that the core was linked with the shell by the chemical bond. The TEM images presented that the core-shell composite particles were all in sphere shape, with smooth surface, well dispersion and uniform size. The diameter of the Ag core was 50±20 nm. The thickness of SiO 2 layer was about 20~30 nm. The thickness of Y 2O 3:RE 3+(RE=Eu, Tb) layer was about 125 nm. The electron diffraction images indicated that Ag@SiO 2@Y 2O 3:RE 3+(RE=Eu, Tb) were polycrystalline structure. The UV-Vis spectra indicated that after surface coating, the plasma resonance absorption peaks of Ag had red shift. The photoluminescence spectra showed that the Ag@SiO 2@Y 2O 3:Eu 3+ samples had characteristic red emission of Eu 3+ and Ag@SiO 2@Y 2O 3:Tb 3+ had characteristic green emission of Tb 3+. But the luminescence intensity was weaker than that of uncoated Y 2O 3:RE 3+ samples, suggesting that the fluorescence of Y 2O 3:RE 3+(RE=Eu, Tb) was quenched by the noble metal.