Understanding the Effect of Al Doping on the Electrochemical Performance Improvement of the LiMn 2 O 4 Cathode Material
Wangqiong Xu,Yonghui Zheng,Yan Cheng,Ruijuan Qi,Hui Peng,Hechun Lin,Rong Huang
DOI: https://doi.org/10.1021/acsami.1c11315
2021-09-17
Abstract:It is well known that the electrochemical performance of spinel LiMn2O4 can be improved by Al doping. Herein, combining X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy, and spherical aberration-corrected scanning transmission electron microscopy (Cs-STEM) with in situ electron-beam (E-beam) irradiation techniques, the influence of Al doping on the structural evolution and stability improvement of the LiMn2O4 cathode material is revealed. It is revealed that an appropriate concentration of Al3+ ions could dope into the spinel structure to form a more stable LiAlxMn2–xO4 phase framework, which can effectively stabilize the surface and bulk structure by inhibiting the dissolution of Mn ions during cycling. The optimized LiAl0.05Mn1.95O4 sample exhibits a superior capacity retention ratio of 80% after 1000 cycles at 10 C (1 C = 148 mA h g–1) in the voltage range of 3.0–4.5 V, which possesses an initial discharge capacity of 90.3 mA h g–1. Compared with the undoped LiMn2O4 sample, the Al-doped sample also shows superior rate performance, especially the capacity recovery performance.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c11315.Rietveld analysis, SEM images and elemental mapping of LiAlxMn2–xO4, corresponding FFT patterns of the HAADF images, variations and fitting curves between Z′ and ω–0.5 in LiMn2O4 and LiAl0.05Mn1.95O4, HAADF images and EDS quantitative results of LiMn2O4 and LiAl0.05Mn1.95O4 samples before and after 1000 cycles at 10 C, thickness distribution results by EELS measurements of LiMn2O4 and LiAl0.05Mn1.95O4 samples, and results obtained from the Rietveld analysis and XPS fitting parameters (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology