Abstract:In this paper, we discussed recent studies done in our laboratories with a floating catalyst chemical vapor deposition (CVD) method. We can grow single- or double-walled carbon nanotubes (SWNTs/DWNTs) with different kinds of catalysts. Single-walled carbon nanotubes without amorphous carbon coating were prepared by thermally decomposing acetylene (C2H2) at the temperature range of 750–1200°C with ferrocene as catalyst. While with sulfur promoted ferrocene catalyst, double-walled carbon nanotubes were mass-produced by pyrolizing C2H2 at the temperature range of 900–1100°C. Furthermore, tunable growth of DWNTs with different diameter was achieved in our experiment. It is found that DWNTs produced at lower carbon partial pressure have much smaller inner tubes, even DWNTs with the smallest inner diameter of 0.4nm was found in here. As convenient and effective tool, radial breathing mode (RBM) of Raman scattering technique can be used to distinguish SWNTs from DWNTs. In further studies of Raman scattering with DWNTs, the possible match of the inner tubes and the outer tubes according to the RBM bands was assigned, and different chirality types were discussed according to the diameter and chirality dependence of resonant Raman vibration. We also investigated the temperature-dependent frequency shift of resonant Raman spectra of DWNTs in the range of 78–650K. We found that different RBM peaks, which are relative to different tube diameters, have different temperature coefficient of frequency shift, and the larger diameter carbon nanotubes have more RBM frequency downshift with increasing temperature. It is ascribed to the RBM frequency variation to the temperature dependence of the stretching force constant of C–C bond. Besides, Polarized Raman spectra were preformed on well-aligned SWNTs structure fabricated through post-growth method and found that the angular dependence of Raman intensity is consistent well with the predictions of the resonance Raman theory.

Outerwall selective alkylcarboxylation and enrichment of double-walled carbon nanotubes

Outer Wall Selectively Oxidized, Water-Soluble Double-Walled Carbon Nanotubes

Diameter-dependent, Progressive Alkylcarboxylation of Single-Walled Carbon Nanotubes

Ultra-clean isotope engineered double-walled carbon nanotubes as tailored hosts to trace the growth of carbyne

(Invited) Efficient Inner-to-Outer Wall Energy Transfer in Highly Pure Double-Wall Carbon Nanotubes Revealed by Detailed Spectroscopy

Direct Enrichment of Metallic Single-Walled Carbon Nanotubes Induced by the Different Molecular Composition of Monohydroxy Alcohol Homologues.

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Two-step Alkylation of Single-Walled Carbon Nanotubes: Substituent Effect on Sidewall Functionalization.

Raman Characterization and Tunable Growth of Double-Wall Carbon Nanotubes

Preparation of Alkyl Functionalized Multi-walled Carbon Nanotubes Using the Esterification of Bromoalkane and Carboxyl Group

Nondestructive and High-Recovery-Yield Purification of Single-Walled Carbon Nanotubes by Chemical Functionalization

Chirally Selective Growth and Extraction of Single-Wall Carbon Nanotubes Via Fullerene Nano-Peapods

Nanopore Structure of Highly Enriched Double-Walled Carbon Nanotube Network Assemblies

Surface Functionalization of Single-Walled Carbon Nanotubes Using Photolysis for Enhanced Dispersion in an Organic Solvent

Controllable preparation and properties of single-/double-walled carbon nanotubes

Enhanced Catalytic Activity of Sub-Nanometer Titania Clusters Confined Inside Double-Wall Carbon Nanotubes.

Reduction of single‐walled carbon nanotube diameter to sub‐nm via feedstock

Reductive Alkylation and Arylation of Single-Walled Carbon Nanotubes in Ethylenediamine Via Benkeser Reaction

Preparation of highly pure double-walled carbon nanotubes

Effective purification of single-walled carbon nanotubes with reversible noncovalent functionalization.

A novel conversion of inert carbon nanotubes to highly dispersed fibres