Abstract:We present a new convenient and efficient "grafting from" method to obtain well defined polystyrene (PS) silica nanoparticles. The method, based on Nitroxide-Mediated Polymerization (NMP), consists to bind covalently the alkoxyamine, which acts as initiator controller agent, at the silica nanoparticles surface in two steps. The first step is a reaction between the aminopropylsilane and the silica particles in order to functionalize the particles surface with amino group. In a second step, the initiating-controlling alkoxyamine moiety is introduced via an over grafting reaction between the amino group and the N-hydroxysuccinimide based MAMA-SG1 activated ester. To simplify both their chemical transformation and the polymerization step, the native silica particles, initially dispersed in water, have been transferred in an organic solvent, the dimethylacetamide, which is also a good solvent for the polystyrene. The synthesis parameters have been optimized for grafting density, conversion rates, and synthesis reproducibility while keeping the colloidal stability and to avoid any aggregation of silica particles induced by the inter-particles interaction evolution during the synthesis. After synthesis, the final grafted objects have been purified and the non-grafted polymer chains formed in the solvent have been washed out by ultra filtration. Then the particles have been studied using Small angle Neutron Scattering (SANS) coupled to neutron contrast variation method. To optimize the contrast conditions, both hydrogenated and deuterated monomers have been used for the synthesis. A refined fitting analysis based on the comparison on two models, a basic core-shell and the Gaussian Pedersen model, enables us to fit nicely the experimental data for both the hydrogenated and deuterated grafted case. Differences are seen between grafting of normal or deuterated chains which can be due to monomer reactivity or to neutron contrast effect variations. The synthesis and the characterization method established in this work constitute a robust and reproducible way to design well defined grafted polymer nanoparticles. These objects will be incorporated in polymer matrices in a further step to create Nanocomposites for polymer reinforcement.

Syntheses of an azo-group-bound silica initiator and silica-polystyrene composites

Poly(L-Lactic Acid)/Sio2 Nanocomposites Via in Situ Melt Polycondensation of L-Lactic Acid in the Presence of Acidic Silica Sol: Preparation and Characterization

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

An Improved Phase-Inversion Process for the Preparation of Silica/Poly[Styrene-Co-(Acrylic Acid)] Core-Shell Microspheres: Synthesis and Application in the Field of Polyolefin Catalysis

Synthesis of SiO<sub>2</sub>/PS composite particles via emulsion polymerization

Synthesis, Characterization, and Properties of Polystyrene/sio2 Hybrid Materials Via Sol–gel Process

Mechanism and Process of the Redispersion of the Aggregated Nano-Sio2 Particles During Emulsion Polymerization of Styrene

Preparation of Carboxyl‐Functionalized Polystyrene/Silica Composite Nanoparticles

In Situ Formation of Silica Nanoparticles Decorated with Well-Defined Homopolymers and Block Copolymers

Morphology and Formation Mechanism of Poly(butyl Acrylate)/nanosilica Composite Particles Prepared by in Situ Emulsion Polymerization

Synthesis of Polystyrene Brushes on Silicate Substrates via Carbocationic Polymerization from Self-Assembled Monolayers

ANCHORING OF AZO INITIATOR AND GRAFTING OF POLY(METHYL METHACRYLATE) ONTO NANAOMETER SILICA

In-situ Emulsion Polymerization of Styrene in the Presence of Nano-Sio2

Grafting of Polystyrene Onto A Nanometer Silica Surface by Microemulsion Polymerization

Synthesis of Silanol-Functionalized Latex Nanoparticles through Miniemulsion Copolymerization of Styrene and γ-Methacryloxypropyltrimethoxysilane

Synthesis, characterization, and properties of polystyrene/SiO2 nanocomposite via sol-gel process

Synthesis of silanol-functionalized latex nanoparticles through miniemulsion copolymerization of styrene and gamma-methacryloxypropyltrimethoxysilane.

Synthesis of SiO2/Polystyrene Nanocomposite Particles Via Miniemulsion Polymerization

Polystyrene grafting from silica nanoparticles via Nitroxide-Mediated-Polymerization (NMP): synthesis and SANS analysis with contrast variation method

One-Step Method for Synthesis of PDMS-Based Macroazoinitiators and Block Copolymers from the Initiators

A Novel In Situ Sol-Gel Synthesis Method for PDMS Composites Reinforced with Silica Nanoparticles