Abstract:Metanilate-layered double hydroxide nanohybrid compound was synthesized for controlled release purposes through co-precipitation method of the metal cations and organic anion. The effect of various divalent metal cations (M2+), namely Zn2+, Mg2+ and Ca2+ on the formation of metanilate-LDH nanohybrids, in which metanilate anion was intercalated into three different layered double hydroxide (LDH) systems; Zn-Al, Mg-Al and Ca-Al were investigated. The syntheses were carried out with M2+ to Al3+ initial molar ratio, R of 4. The pH of the mother liquor was maintained at pH 7.5 and 10 during the synthesis, and the resulting mixture was aged at around 70 degrees C for about 18 h. The intercalation of metanilate anion into the host was found to be strongly influenced by the M2+ that formed the inorganic metal hydroxide layers. Under our experimental condition, the formation of the nanohybrid materials was found to be more feasible for the Zn-Al than for the other two systems, in which the former showed well-ordered layered organic-inorganic nanohybrid structure with good crystallinity. Intercalation is confirmed by the expansion of the interlayer spacing to about 15-17 A when metanilate was introduced into the interlamellae of Zn-Al LDHs. In addition, CHNS and FTIR analyses also support that metanilate anion has been successfully intercalated into the interlamellae of the inorganic LDH. Apart from M2+, this study also shows that the initial pH of the mother liquor plays an important role in determining the physicochemical properties of the resulting nanohybrids, especially the mole fraction of the Zn2+ substituted by the Al3+ ion in the LDH inorganic sheets which in turn controlled the loading percentage of the organic anion, surface properties and the true density. Preliminary study shows that LDH can be used to host beneficial guests, active agent with controlled release capability of the guests. Generally the overall process is governed by pseudo second order kinetic but for the first 180 min, the release process can be slightly better described by parabolic diffusion than the other models.

Effect of Metal Ion Concentration on the Property of Methotraexate/Layered Double Hydroxide Compounds

Facile synthesis of methotrexate intercalated layered double hydroxides: particle control, structure and bioassay explore

Methotrexate intercalated layered double hydroxides with different particle sizes: structural study and controlled release properties

Effect of Binding Affinity of Crystal Water on the Electrochemical Performance of Layered Double Hydroxides.

Effect of Corrosion Inhibitor Pyrovanadate Ions on Microstructure and Corrosion Resistance of MgAl Layered Double Hydroxide Films on LA43M Mg-Li Alloy

Effect of different anion intercalations on the corrosion resistance of layered double hydroxides on the surface of LA43M

Effect of Microstructure on Layered Double Hydroxides Film Growth on Mg-2Zn-xMn Alloy

Enhanced Corrosion Resistance and Biocompatibility of Magnesium Alloy by Mg-Al-Layered Double Hydroxide

Preparation and corrosion behavior of Mg(Li)-M layered double hydroxides films on the surface of magnesium-lithium alloy

Controlled release compound based on metanilate-layered double hydroxide nanohybrid

Regulation of Structure and Anion-Exchange Performance of Layered Double Hydroxide: Function of the Metal Cation Composition of a Brucite-like Layer

Selective Covalent Basal Plane Modification as a Probe of Hydroxide Ion Conduction Pathways in Magnesium Aluminum Layered Double Hydroxides

Influences of Cation Ratio, Anion Type, and Water Content on Polytypism of Layered Double Hydroxides.

Effect of Divalent Metals on the UV-Shielding Properties of MII/MgAl Layered Double Hydroxides.

Comparative Study on Corrosion Resistance of Binary and Ternary Layered Double Hydroxide Films on Magnesium Lithium Alloy

Stability Trends in Mono-Metallic 3d Layered Double Hydroxides

Long-Range and Short-Range Structures of Multimetallic Layered Double Hydroxides

Effects of Surface Pretreatment on Structure and Release Performances of Mg-Al Hydrotalcites

Influence of Mg substrate on the formation mechanism and corrosion resistance of LDH films

Microstructure, Corrosion Resistance, and Antibacterial Properties of an Ag/Mg-Al Layered Double Hydroxide Coating Synthesized in Situ on Biomedical Mg-Zn-Ca Alloy

Insights into cellular interactions of characterized Mg-Al Layered Double Hydroxide on L929 cells