Abstract:Bimetallic Cu-ZnO-based catalyst were systematically prepared via impregnation technique under controlled synthesis conditions of active metal loading, ratio of active metal Cu:Zn and synthesis pH. The effect of the synthesis condition on the performance of the Cu-ZnO supported catalysts with respect to the hydrogenation of CO 2 to methanol in micro-activity fixed-bed reactor at 250°C, 2.25 MPa, and 75% H 2 /25%CO 2 ratio. The synthesized catalysts were characterized by transmission electron microscopy (TEM) and temperature programmed desorption, reduction, oxidation and pulse chemisorption (TPDRO) and the surface area determination was also performed. The results demonstrate that the catalytic structure, activity, and methanol selectivity was strongly affected by the synthesis parameters. Increasing of synthesis pH from 1 to 7 shows better metal particles distribution, Cu desperation of 29%, higher BET surface area as well as Cu surface area, while further increasing on pH revealed on particles agglomeration and weak metal-support interaction. In addition, increasing of the active metal loading from 5 to 15 % resulted in dramatic increase in the conversion of CO 2 and methanol production while further increase caused lower catalytic performance. Moreover, catalyst with total loading of 15%, Cu:Zn ratio of 70:30 synthesized at pH of 7 exhibit higher catalytic activity of 14%, methanol selectivity of 92%, and TOF of 1.24×10 3 s -1 compared with other catalyst prepared under various conditions

Effect of Promoter TiO2 on the Performance of CuO-ZnO-Al2O3 Catalyst for CO2 Catalytic Hydrogenation to Methanol

Effect of Promoter SiO2, TiO2 or SiO2-TiO2 on the Performance of CuO-ZnO-Al2O3 Catalyst for Methanol Synthesis from CO2 Hydrogenation

Theoretical Investigation on the CO2 Hydrogenation to Methanol Mechanism at Electron-Rich Active Interface over Cu/Ga-Ti-Al-O Catalyst

Effect of Promoters on Catalytic Performance for CO2 Hydrogenation to Methanol

Effects of ZrO2-promoter on Catalytic Performance of CuZnAlO Catalysts for Production of Hydrogen by Steam Reforming of Methanol

Promoting effect of titanium on Cu/γ-Al2O3 catalyst for CO2 hydrogenation

Characterization and Catalytic Performance Study of CuO-ZnO-ZrO2-TiO2 Catalyst for Methanol Synthesis from Carbon Dioxide Hydrogenation

Promoting effect of titanium on Cu/gamma-Al2O3 catalyst for CO2 hydrogenation

Modulation of Al2O3 and ZrO2 composite in Cu/ZnO-based catalysts with enhanced performance for CO2 hydrogenation to methanol

Influence of Cu/Al Ratio on the Performance of Carbon-Supported Cu/ZnO/Al2O3 Catalysts for CO2 Hydrogenation to Methanol

Cu/ZnO/Al2O3 Catalyst Modulated by Zirconia with Enhanced Performance in CO2 Hydrogenation to Methanol

High-Performance Cu/ZnO/Al 2 O 3 Catalysts for CO 2 Hydrogenation to Methanol

Formic Acid Assisted Synthesis of Cu-ZnO-Al2O3 Catalyst and Its Performance in CO2 Hydrogenation to Methanol

Comparative Study on the Effect of Cerina and Alumina on the Catalytic Activity of CuO-ZnO Based Catalyst in CO2 Hydrogenation to Methanol

Effect of Cu and Zn on the performance of Cu-Mn-Zn/ZrO2 catalysts for CO2 hydrogenation to methanol

Yttria-doped Cu/ZnO Catalyst with Excellent Performance for CO2 Hydrogenation to Methanol

Effects of Zro2 on the Performance of Cuo-Zno-Tio2-Zro2 Catalysts Used in Methanol Synthesis from Co2 Hydrogenation

Effect of Oxide Coating on Performance of Copper-Zinc Oxide-Based Catalyst for Methanol Synthesis via Hydrogenation of Carbon Dioxide

Catalytic Hydrogenation of CO2 to Methanol: Study of Synergistic Effect on Adsorption Properties of CO2 and H2 in CuO/ZnO/ZrO2 System

Effect of Catalyst Synthesis Parameters on the Performance of CO2 Hydrogenation to Methanol over SBA-15 Supported Cu/ZnO-Based Catalysts