Abstract:The currently used low carbon operation in blast furnaces (BFs) leads to a thin coke layer and deterioration in gas and liquid permeability. Previous studies have reported that coke breeze, formed by the graphitization of coke, is one of the main influences on gas and liquid permeability in the high-temperature zone of a BF. To investigate the influence of the graphitization of BF coke on its metallurgical properties, the degree of coke graphitization under different heating temperatures from 1100 to 1500℃ was investigated. The dependence of the degree of graphitization on coke reactivity index (CRI) and coke strength after reaction (CSR) was also studied. The relationship between different degrees of graphitization in coke and alkali metals was clarified. Finally, the micro-morphology of coke was inspected and analyzed. Results show that with increasing temperature, the degree of coke graphitization intensifies. With every 100℃ rise in heating temperature, the degree of coke graphitization increases 1.8 times, the value of the spacing of layers (d002) decreases by 2%, and the values of the layers diameter of microcrystalline structure (La) and the stack height (Lc) are improved by 3% and 15%, respectively. In addition, it is observed that the surface stomata of the coke decreases particularly the large pores, the mosaic structure decreases, the isotropic structure increases, and the degree of structural ordering increases. When the degree of graphitization intensifies, the CRI of the coke gradually decreases, the CSR gradually increases, the degree of coke degradation weakens, the formed large pores reduced, and the trend for pore wall damage is reduced. Moreover, the alkali metal plays a catalytic role in improving the CRI and decreasing the CSR. It is considered that the graphitized coke resists the destruction of the alkali metal and thus decreases the degree of coke degradation.

Structure Changes and Gasification Activity of Petroleum Coke after Heat Treatment

Effect of Heat Treatment on Structure and Gasification Reactivity of Petroleum Coke

In-situ gasification characteristics of a petroleum coke with CO2 at high temperature

Effect of high-temperature pyrolysis on the structure and properties of coal and petroleum coke

Effect of Microwave Treatment on Structural Changes and Gasification Reactivity of Petroleum Coke

Combustion and gasification properties of petroleum coke and its pyrolytic semi-coke

Changes in the Microstructure and Gasification Reactivity of Petroleum Coke and Coal Samples after Rapid Pyrolysis

PHYSICAL STRUCTURES AND CO2 GASIFICATION CHARACTERISTICS OF PETROLEUM COKE AND PITCH COKE AT THE CONDITION OF HIGH TEMPERATURE CALCINATION

MICROCRYSTALLITE STRUCTURAL CHANGES OF PETROLEUM COKE DURING THE COURSE OF CARBONIZATION ANALYZED BY X-RAY DIFFRACTION

Effect of blast furnace coke graphitizing its high temperature metallurgical properties

Experimental study on co-gasification of coal liquefaction residue and petroleum coke

Structural characteristics and flammability of low-order coal pyrolysis semi-coke

Synergistic Effect on Co-Gasification Reactivity of Biomass-Petroleum Coke Blended Char

Effect of Microwave Activation on the Characteristics of Petroleum Coke Gasification

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

The coking performance of petroleum and coal-based products - II. Influence of coking conditions

Characteristics of single petcoke particle during the gasification process at high temperatures

Effect of gasification reaction on pore structure, microstructure, and macroscopic properties of blast furnace coke

Effect of catalysts on the reactivity and structure evolution of char in petroleum coke steam gasification

Comparative Study on Devolatilization Behavior, Microstructural Evolution and Resultant Properties During Calcination of Petroleum Coke with Distinct Mesophase Texture

Differences in Physical Properties and CO2 Gasification Reactivity Between Coal Char and Petroleum Coke