Abstract:Soft coal tar pitch (SCTP) with low QI content is the preferred raw material for preparing coal-based needle coke, the study on its structure changes in the stage of liquid-phase carbonization into coke (350 similar to 550 degrees C) is helpful to prepare high-quality needle coke. In this paper, a detailed analysis on the C-H stretching vibration peaks in the range of 3 100 similar to 2 800 cm(-1) and the aromatic C-H bending vibration peaks in the range of 900 similar to 700 cm(-1) has been carried by the peak-fitting technique using the infrared spectra of the sample. And then based on the calibration factors of the corresponding C-H vibration peaks for the stand- ard substances, the mass percentages of the different types of aromatic hydrogen (H-solo , H-duo, H-trio and H-quarto) and aliphatic hydrogen (H-CH3, H-CH2 and H-CH) of SCTP were quantitated at different carbonization temperatures (400, 500, 600 and 800 degrees C). Furthermore, the contents of SP2 hybridized Carbon ((SPC)-C-2) and SP3 hybridized Carbon ((SPC)-C-3) as well as these structural parameters such as H/C atomic ratio, aromatic index (I-ar) , aromatic ortho-substitution index (I-os) and branched index (CH3/CH2) were calculated, and the changes of aromatic structure of SCTP during the coking process were also discussed. The results showed that the coal-based needle coke raw material SCTP is mainly composed of aromatic hydrocarbons with a low number of the ring and few side chains, its I(ar )is 0. 77, and about 82% of its aromatic hydrogen is distributed in the structure containing three/four adjacent aromatic C-H, while its aliphatic hydrogens are mainly distributed in the CH2 of naphthenic structures. With the increase of carbonization temperature, the aliphatic hydrogen or (SPC)-C-3 of SCTP decreased almost linearly, losing about 50% at 400 degrees C , which was mainly attributed to the loss of light components and the dehydrogenation of naphthenic structures. The green coke formed at 500 degrees C had Only 0. 15 Wt. % aliphatic hydrogen and 0. 88 Wt. % SP3 C, and the presence of aliphatic hydrogen was not detected at 600 degrees C. However, the aromatic hydrogen increased slightly from 3. 89 Wt. % of the raw material to 4. 5 Wt. % before 400 degrees C because of the conversion of the naphthenic structuresinto aromatic rings. As the temperature increases further, aromatic hydrogen decreases rapidly, reaching only 1. 14 Wt. % when the temperature reaches 500 degrees C , indicating that the aromatic hydrocarbon molecules undergo intense dehydrogenation condensation reaction during the mesophase formation stage at 400 similar to 500 degrees C , which was also confirmed by the conversion of a large number of protonated (SPC)-C-2 into unprotonated (SPC)-C-2. Aromatic hydrogen continued to decrease after 500 degrees C , and their presence was not detected at 800 degrees C. In addition, it was found that the out-of-planebending vibration of aromatic C-H is more sensitive to infrared light than its in-plane stretching vibration. The increase of I-ar and the decrease of these parameters such as H/C atomic ratio, I-os, CH3/CH2, indicated that the aromatic molecules in the SCTP are gradually grown up by their condensation, and its aromaticity increased in the coking process. The fast quantification of various types of hydrogen by infrared spectrum can timely understand the structural changes of aromatic hydrocarbon molecules of the pitch in the coking process, which is helpful to the production of needle coke.

MICROCRYSTALLITE STRUCTURAL CHANGES OF PETROLEUM COKE DURING THE COURSE OF CARBONIZATION ANALYZED BY X-RAY DIFFRACTION

Evolution of Coke Microstructure and Metallurgical Properties During Graphitization in a Blast Furnace

Pore Structure Evolution During the Coke Graphitization Process in a Blast Furnace

Effect of high-temperature pyrolysis on the structure and properties of coal and petroleum coke

Chemical-structural Properties of the Coke Produced by Low Temperature Oxidation Reactions During Crude Oil In-Situ Combustion

Mechanism of carbon structure transformation in plastic layer and semi-coke during coking of Australian metallurgical coals

A comprehensive investigation on the structural transformation and dissolution loss reaction of coke during gasification in CO 2 atmosphere

Combustion and gasification properties of petroleum coke and its pyrolytic semi-coke

Changes of specific pore surface area and pore volume of petroleum coke during combustion

Effect of blast furnace coke graphitizing its high temperature metallurgical properties

Changes in Functional Groups and Crystal Structure of Coal Tar Pitch with Respect to Carbonization Temperature

Infrared Spectroscopic Quantitative Analysis of Raw Material Used As Coal-Based Needle Coke in the Coking Process

Differences and correlations between microstructure and macroscopic properties of mesophase cokes derived from the components of high temperature coal tar pitch

Effects of co-carbonization of medium and low temperature refined pitch and high temperature refined pitch on the structure and properties of needle coke

Impact of Chemical Structure of Coal on Coke Quality Produced by Coals in the Similar Category

Effects of Fe2O3 addition on the thermoplasticity and structure of coking coal matrix during thermoplastic stage of pyrolysis

Co-carbonization Behaviors of Petroleum Pitch/waste SBS: Influence on Morphology and Structure of Resultant Cokes

Experiment on thermal cracking coke of aviation kerosene

Structural characteristics and flammability of low-order coal pyrolysis semi-coke

In-situ study of the heating rate effects on covalent bonds conversion and pore/carbon microcrystal evolutions of coal molecule during coking

Pore Structure and Fractal Characteristic Analysis of Gasification-Coke Prepared at Different High-Temperature Residence Times