Ion irradiation induced order-to-disorder transformations in δ-phase Sc4-xZr3+xO12+ x/2

Jiachi Zhang,Yongqiang Wang,Ming Tang,James James Valdez,Kurt E. Sickafus

DOI: https://doi.org/10.1016/j.nimb.2010.05.031

2010-01-01

Abstract:The purpose of this study is to investigate the role of stoichiometry on crystal structure transformations in derivative fluorite compounds known as delta (δ) phase. In this study, polycrystalline δ-phase ceramic pellets were prepared with stoichiometries given by Sc4−xZr3+xO12+x/2 (x=0, 0.77 and 1.20). The pressed and polished pellets were then irradiated under cryogenic conditions with 200keV Ne+ ions to fluences ranging from 1–5×1014Ne/cm2. An order–to–disorder (O–D) transformation was observed for all compositions, as determined using grazing incidence X-ray diffraction (GIXRD). However, the transformation threshold dose was found to systematically decrease with increasing ZrO2 content: ∼0.2, ∼0.16, and ∼0.08dpa for Sc4−xZr3+xO12+x/2 with x=0, 0.77, and 1.20, respectively. These irradiation-induced phase transformation results are discussed in terms of the crystal structure of the δ-phase.