Initial Stages of Ion Beam-Induced Phase Transformations in Gd2O3 and Lu2O3

Chien-Hung Chen,Cameron L. Tracy,Chenxu Wang,Maik Lang,Rodney C. Ewing

DOI: https://doi.org/10.1063/1.5013018

IF: 4

2018-01-01

Applied Physics Letters

Abstract:The atomic-scale evolution of lanthanide sesquioxides Gd2O3 and Lu2O3 irradiated with 1 MeV Kr ions at room temperature and 120 K, up to fluences of 1 × 1016 ions/cm2 (∼20 dpa), has been characterized by in situ transmission electron microscopy. At room temperature, both oxides exhibited high radiation tolerance. Irradiation did not cause any observable structural change in either material, likely due to the mobility of irradiation-induced point defects, causing efficient defect annihilation. For Gd2O3, having the larger cation ionic radius of the two materials, an irradiation-induced stacking fault structure appeared at low fluences in the low temperature irradiation. As compared with the cubic-to-monoclinic phase transformations known to result from higher energy (∼GeV) ion irradiation, Kr ions of lower energies (∼MeV) yield much lower rates of damage accumulation and thus less extensive structural modification. At a fluence of 2.5 × 1015 ions/cm2, only the initial stages of the cubic-to-monoclinic (C to B) phase transformation process, consisting of the formation and aggregation of defects, have been observed.