Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Shape-Controlled Synthesis and Related Growth Mechanism of Pb(OH) 2 Nanorods by Solution-Phase Reaction

Controllable synthesis and growth mechanism of α-Co(OH)2 nanorods and nanoplates by a facile solution-phase route

Selected-Control Synthesis of PbO2 and Pb3O4 Single-Crystalline Nanorods

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Controllable Chemical Reaction Synthesis of Tb(OH)3 Nanorods and Their Photoluminescence Property

Efficient synthesis of dendritic PbTiO3 nanorods by hydrothermal method

Synthesis and Characterization of Single Crystalline PbO Nanorods Via a Facile Hydrothermal Method

Synthesis and the Growth Mechanism of PbS Nanorod

Shape Evolution Of Pb (Zr,Ti)O-3 Nanocrystals Under Hydrothermal Conditions

Synthesis and characterization of beta-PbO2 nanorods and Pb3O4 nanocrystallites

Hydrothermal Synthesis and Phase-, Morphology-Evolution Mechanism of Lead Titanate Nanostructures Assisted with Tetramethylammonium Hydroxide

Morphology control of one-dimensional lead hydrogen phosphate nanostructures synthesized by a solution route

Hydrothermal Synthesis of Lead Zirconate Titanate Nearly Free-Standing Nanoparticles in the Size Regime of about 4 Nm

Controlled Synthesis of PbWO4 Dendrites by a Simple Sonochemical Method

Growth Mechanism And Properties Of Zno Nanorods Synthesized By Plasma-Enhanced Chemical Vapor Deposition

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

Polymer‐Assisted Hydrothermal Synthesis of Single‐Crystalline Tetragonal Perovskite PbZr0.52Ti0.48O3 Nanowires

Synthesis of Single-Crystal PbS Nanorods Via a Simple Hydrothermal Process Using PEO-PPO-PEO Triblock Copolymer As a Structure-Directing Agent.

Controllable Growth of In(OH)(3) Nanorods with Rod-in-rod Structure in a Surfactant Solution

Controlled Synthesis Of Pbte Nanorods And Nanotubes

Shape and size control of ZnO nanostructures via a simple solution route.