Abstract:In the literature, there is only one publication on the experimental isothermal section at 773 K in the Al-Er-Zr system, and no information is available on solidification microstructure in this system. Solidification paths and phase equilibria of the Al-Er-Zr ternary system at 873 and 673 K were thus investigated by means of 14 alloys using X-ray diffraction (XRD), scanning electron microscope (SEM) and electron probe micro analysis (EPMA). Ten primary phases were revealed and two isothermal sections at 873 and 673 K were established in this work. There are fourteen ternary-phase regions at two temperatures and the topology of phase relations is identical at both temperatures. It is found that the maximal solubilities of Er in Al3Zr, Al2Zr, Al3Zr2, AlZr, Al3Zr4, Al2Zr3, AlZr2 and AlZr3 are 2.2 ± 0.1, 4.5 ± 0.2, 9.8 ± 0.5, 11.8 ± 0.6, 8.6 ± 0.3, 6.8 ± 0.3, 4.8 ± 0.2 and 4.4 ± 0.2 at%, respectively. In addition, there are also noticeable solubilities for Zr in Al-Er binary compounds (i.e., Al3Er, Al2Er, AlEr, Al2Er3 and AlEr2), and the maximal solubility of Zr in Al2Er3 is up to 18.0 ± 0.9 at% at 673 K. The phase equilibria and solidification paths in the Al-Er-Zr system determined in the present work provide new experimental data for a future thermodynamic assessment of this system.

Phase Equilibria in the Al–Zr–Ce System at 773 K

Experimental Study of Al–Zr–Y System Phase Equilibria at 773 K

Phase Diagrams of the Ce-Si-Zr Ternary System at 773 and 1173 K

Phase equilibria of the Al-Pr-Zr ternary system at 773 K

Phase Equilibria of the Er-Al-Zr Ternary System at 500 °C

Experimental Phase Diagram of the Al-Er-Zr Ternary System

The Phase Equilibria of the 75 at.% Al-Zn-Ce-Fe Quaternary System at 600 °C

Phase equilibria in the ternary Al–Zr–La system

Phase Relationships in the Al-rich Region of the Al-Y-Zr System

Experimental Investigation of the Phase Equilibria of the Zn-Al-Zr Ternary System at 723 K (450 °C)

Phase Equilibria of the Ag–Zn–Ce (0–33.3 At.% Ce) System at 450 °C and 600 °C

Solidification paths and phase equilibria at 873 and 673 K in the Al-Er-Zr system

Isothermal Section of the Al–Dy–Zr Ternary System at 773 K

Phase Equilibria of the Al-Sc-Zr Ternary System at 500 °C

Experimental investigation of the phase equilibria of the Al-Ce-Ge system at 500 ℃

Isothermal Section of Al-Si-Ce Ternary System at 1073 K

Experimental Investigation of Phase Equilibria in the Zr–Cu–Al System

Phase Relationships in the Zn-Rich Corner of the Zn-Fe-Zr System

Phase Diagram of the Al–Dy–Zr Ternary System at 773 K

The Phase Equilibria of the Al–Ce–Ni System at 500°C

Determination of the Phase Equilibria in the Al–Er–V Ternary System at 773 K