Abstract:Hot compression tests of Al-Zn-Mg alloy containing small amount of Sc and Zr were carried out on a Gleeble-1500 thermo-mechanical simulator in deformation temperature range from 340 to 500 degrees C and at strain rate range from 0.001 to 10s (1). The microstructural evolution and flow behavior of the alloy under various conditions were investigated. It was observed that the flow stress increased with increasing strain rate and decreasing deformation temperature, the main dynamic soften mechanism was caused by dynamic recovery and dynamic recrystallization. Based on the experimental results, Arrhenius- type constitutive equations and artificial neural network (ANN) model with a back-propagation learning algorithm were established to predict hot deformation behavior of the alloy. A comparative predictability of constitutive equations and ANN model were further evaluated using a wide variety of statistical indices. The average absolute relative error was 0.58% and 3.57% corresponding to ANN model and constitutive equations, respectively. The relative errors between experimental and predicted flow stress computed from constitutive equations and ANN model were respectively in the range of 15.58% to -15.32% and 3.16% to -3.25%. The results showed that the predicted flow stresses by ANN model were in a better agreement with experimental values, indicating that ANN model is more accurate and efficient than Arrhenius-type constitutive equations. (c) 2013 Elsevier B.V. All rights reserved.

Hot compression deformation behavior of ZK60 magnesium alloy based on artificial neural network

Artificial Neural Network Modeling to Evaluate and Predict the Deformation Behavior of Zk60 Magnesium Alloy During Hot Compression

Hot Compression Behavior and Flow Stress Prediction of Zk60 Magnesium Alloy

Hot compression behavior of ZK60 magnesium alloy

Hot compression deformation behavior of extruded ZK60 magnesium alloy

Prediction Flow Behaviour of a Magnesium Alloy in Hot Deformation and a Comparative Study by Using Hyperbolic Sine Model and ANN Model

Constitutive modeling for elevated temperature flow behavior of ZK60 magnesium alloy

Study of Hot Compression Behavior of ZK60 Magnesium Alloy at Elevated Temperature

Modeling of strain hardening and dynamic recrystallization of ZK60 magnesium alloy during hot deformation

Modeling of Flow Stress Considering Dynamic Recrystallization for Magnesium Alloy ZK60

Flow Stress Behavior of ZK60 and Al18B4O33w/ZK60 During Hot Compression Deformation at Elevated Temperature

Flow Behavior of Al–6.2Zn–0.70Mg–0.30Mn–0.17Zr Alloy During Hot Compressive Deformation Based on Arrhenius and ANN Models

Thermal simulation on hot deformation behavior of ZK60 and ZK60(0.9Y) magnesium alloys

Hot Deformation Behaviors of AZ91 Magnesium Alloy: Constitutive Equation, Ann-Based Prediction, Processing Map and Microstructure Evolution

Flow characterization of magnesium alloy ZK61 during hot deformation with improved constitutive equations and using activation energy maps

Microstructural Evolution and Constitutive Relationship of Al–Zn–Mg Alloy Containing Small Amount of Sc and Zr During Hot Deformation Based on Arrhenius-type and Artificial Neural Network Models

Hot Deformation Behavior and Workability of Pre-Extruded ZK60A Magnesium Alloy

Characterization of hot deformation behavior of extruded ZK60 magnesium alloy using 3D processing maps

Artificial neural network prediction to the hot compressive deformation behavior of Al–Cu–Mg–Ag heat-resistant aluminum alloy

Modeling of Flow Stress for Magnesium Alloy During Hot Deformation

Modeling the Hot Deformation Behaviors of As-Extruded 7075 Aluminum Alloy by an Artificial Neural Network with Back-Propagation Algorithm