Preparation and Characterization of Bio-Medical Porous Titanium by Unconventional Powder Metallurgy

ZOU Hui,LU Qi,TIAN Wei-dong,LIU Ying,LIAN Li-xian,SHI Bo
DOI: https://doi.org/10.3969/j.issn.1007-4252.2010.05.014
2010-01-01
Abstract:Porous titanium for biomedical applications was prepared by spark plasma sintering(SPS) technology,using atomized pure titanium powders as raw material and ammonium bicarbonate as space holder.Its phase composition and micro-morphology were analyzed by XRD and SEM,respectively.Mechanical properties and biocompatibility were also investigated.By adjusting the content of space holder and controlling process parameters,specimens can be obtained with porosities in the range of 50.3%~70.5% and pore diameters in the range of 100~300μm,whose compressive strength(24.40~68.96MPa) and elastic modulus(1.010~1.287GPa) are similar to those of human cancellous bone.Rat osteoblasts can adhere to rough surface and grow into porous structure after co-cultured with porous titanium discs in vitro for 2 days,indicating that such material has good biocompatibility.
What problem does this paper attempt to address?