Properties and Fabrication of Biomedical Porous Ti by Spark Plasma Sintering

SHI Bo,LIU Ying,LIAN Li-xian,ZHOU Hui,SUN Wei-ze,GENG Zheng-wei,WANG Cheng
DOI: https://doi.org/10.3321/j.issn:1001-9731.2009.11.037
2009-01-01
Abstract:Three-dimensional connective porous titanium was prepared by spark plasma sintering,using biomedical atomized spherical Ti powder as raw material and polyurethane foam as a template. Then the samples were tested by XRD,SEM,and compression experiments machine. The results showed that the porous samples were pure titanium and their pore sizes were in the range of 100-500μm,with their porosities in the range of 72.5%-83%.The compressive strength and elastic modulus were in the range of 10.3-51.8MPa and 0.32-1.25GPa,respectively. These values were similar to reticular bone. The experiment of bone-phosphate deposition showed that the porous titanium was bioactive.