Probabilistic analysis on crack growth life of turbine disk under lcf-creep through experimental data

Dianyin Hu,Rongqiao Wang,Jiang Fan,Xiuli Shen

2010-01-01

Abstract:Fatigue durability and inspection planning have long been important issues in the design and scheduled inspection of the aero-engines. Usually, the turbine disk acting as one of the most important structures of the aero-engine has to be designed for a finite life with an accepted probability of failure based on the S-N approach. Hence, cracks may propagate and become critical during the predicted “safe-life”, unless discovered in time and repaired. The crack growth life of turbine disks at elevated temperatures is governed by the modes of degradation and failure including low cycle fatigue (LCF) failure and creep failure. Meanwhile, uncertainties related to the operating environment (speed, temperature, etc.) as well as in the structural properties (material properties, geometries, boundary conditions etc.), can result in considerable statistical scatter in the turbine disk life. The need for cost-effective designs has resulted in the development of probabilistic analysis to quantify the effects of these uncertainties to improve the components’ reliability. Thus the purpose of this paper is to carry out a probabilistic analysis on crack growth life of turbine disk under LCF-creep based on experimental results. First, an experimental system to achieve real-time fatigue-creep crack growth(FCCG) detection at high temperature is established by introducing a long-distance microscope with high magnification and resolution from distances of 15cm to 35cm. This setup consists of a dynamic testing machine, a machine controller, a temperature controlled box, a long-distance microscope and a high temperature furnace from room temperature to 1000 . °C Then the FCCG rate tests on 30 compact tension (CT) specimens made of GH4133B material at 600 are carried out. T °C he tests are conducted on a 100KN capacity servo-hydraulic closed-loop machine employed trapezoidal load with hold time at upon peak load. Experiments on the fatigue crack growth have shown great dispersancy. The deterministic model for FCCG rate fitted by SINH model, which considers the parameters including temperature, hold time is established through experimental data. And the stochastic FCCG model for GH4133B is proposed and the probability of random time to reach a specified crack size can be obtained as well as the distribution function of crack size at the service time. Through comparison between the analytical and experimental results, it’s found that the probabilistic FCCG model can fit the experimental data well. Once the stochastic FCCG model is established, it can be used for the probabilistic damage tolerance analysis and design of the turbine components made of GH4133B material. At last, considering random characteristics of material parameters and load including rotational speed and temperature, a failure function is established based on the stochastic FCCG model. Then the centroidal Voronoi tessellation (CVT) sampling is used to improve the efficiency. The probabilistic methods of response simulation and Monte Carlo method are employed to carry out the probabilistic PROBABILISTIC ANALYSIS ON CRACK GROWTH LIFE OF TURBINE DISK UNDER LCF-CREEP THROUGH EXPERIMENTAL DATA