The phase structure and electrochemical properties of the melt-spun alloy Zr0.7Ti0.3Mn0.4V0.4Ni1.2
S.K Zhang,Q.D Wang,Y.Q Lei,G.L Lü,L.X Chen,F Wu
DOI: https://doi.org/10.1016/S0925-8388(01)01482-7
IF: 6.2
2002-01-01
Journal of Alloys and Compounds
Abstract:The crystal structure, phase abundance, microstructure and electrochemical properties of the AB(2)-type Laves phase hydrogen storage alloy Zr0.7Ti0.3Mn0.4V0.4Ni1.2 were studied, prepared both by arc-melting and melt-spinning. The XRD patterns have revealed that two Laves phases, C14 and C15 are formed in the as-cast alloy. In the melt-spun alloy, besides the C14 and C15 phase in very fine crystal grains, there appears a new crystalline C14 phase with very fine crystallites, which is named the nanocrystallite C14 in this paper. SEM and EDS analyses have indicated that the microstructure of melt-spun alloy is a very fine dendritic structure (10 x 3 mum), while the as-cast alloy is a much coarser dendritic structure (300 x 50 mum) with noticeable composition segregation. Electrochemical tests have indicated that the melt-spun alloy has a higher discharge capacity of 385 mA h g(-1) in comparison with 371 mA h g(-1) for the as-cast alloy and the melt-spun alloy has very good cycling stability. After 500 cycles, 80.7% of the initial discharge capacity is retained, much higher than 63.1% of the as-east alloy. It is thus inferred that the electrochemical capacity of the nanocrystallite C14 phase is higher than that of the conventional C14 phase. Nevertheless, the activation property and the high-rate dischargeability of the melt-spun alloy were both found to decrease noticeably, most probably due to the higher resistance against decrepitation and cracking of the alloy with a more refined grain structure. (C) 2002 Elsevier Science B.V. All rights reserved.