Abstract:Traditional CPC cements have attracted wide attentions in repairing bone defects for injectability, easy plasticity and good osseointegration. However, its further application was limited by poor mechanical properties, long setting time and unsatisfactory biocompatibility. To solve these problems, polydopamine (DOPA) coated strontium-doped calcium polyphosphate (SCPP) fibers were added into CPC cements for the first time. A doping amount at fiber weight fraction of 0%, 1%, 2% and 5% was designed to develop a multifunctional composite fitting for bone tissues' regeneration and reconstruction and the optimum amount was selected through subsequent physicochemical and biological characterizations. The results implied DOPA coating successfully formed stable connections between SCPP fibers and CPC matrix, which simultaneously reinforced biomechanical strength and tenacity (5% SCPP/D/CPC samples exhibited more prominent mechanical property than others). In addition, 5% D/SCPP fibers doped composite cements were characterized as markedly-improved cytocompatibility: Sr2+ introduction induced cytoactive and significantly accelerated proliferation, attachment and spreading of osteoblasts. Besides, it also stimulated the secretion of OT, Col-I and ALP from seeded MG63, which was a critical character for further inducing osteogenic process, mineralization and bone tissues formation. The promoted cytocompatibility and improved osteogenesis-related growth factors' secretion could be attributed to constant and controllable release of Sr2+ and this deduction was approved by ICP analysis. In addition, Sr doping made this novel cement had a potential efficacy to inhibit aseptic loosening. In a word, present studies all demonstrated 5% SCPP/D/CPC composites could be a potential candidate material employed in bone regeneration and reconstruction for excellent mechanical property and cytocompatibility.

Optimization and Characterization of Injected Β-Tcp CPC

Preparation and performance of CPC/eucommia ulmoides Oliv.composites

A type of injectable porous calcium phosphate cement in vivo

Preparation and Characterization of Injectable Calcium Phosphate Cement Paste Modified by Polyethylene Glycol-6000

Preparation of CPC Carried by Eucommia Ulmoides Oliv. Extracts

Research Progress on the Physicochemical Properties of Improved CPC

Preparation and characterization of calcium phosphate cement with enhanced tissue adhesion for bone defect repair

Synthesis and property of a novel calcium phosphate cement.

Preparation of a novel calcium phosphate cement using N-methylene phosphonic chitosan as a gelling agent

Study on the applied properties of tobramycin-loaded calcium phosphate cement

Study on the Improvement of Compressive Strength and Fracture Toughness of Calcium Phosphate Cement

Preparation and Properties of Injectable Hydroxyapatite for Bone Repair Materials

A novel injectable calcium phosphate cement-bioactive glass composite for bone regeneration

Study on Cpc Carried by Rhbmp-2

In vitro and in vivo analysis of the biocompatibility of two novel and injectable calcium phosphate cements.

Improved Injectability and in Vitro Degradation of a Calcium Phosphate Cement Containing Poly(lactide-Co-glycolide) Microspheres.

Rheological properties of concentrated aqueous injectable calcium phosphate cement slurry.

Development of calcium phosphate cement and analysis

Octacalcium phosphate phase forming cements as an injectable bone substitute materials: Preparation and in vitro structural study

Preparation of Hydroxyapatite Cement and Analysis As of Its Disposition

A Novel CPC Composite Cement Reinforced by Dopamine Coated SCPP Fibers with Improved Physicochemical and Biological Properties.