Abstract:Mg-10Gd-3Y-1.8Zn-0.5Zr (mass fraction, %) (GWZ1032K) alloys were fabricated by permanent mold casting and slow solidification with different cooling rates. The microstructures of the GWZ1032K alloys with different cooling rates were investigated by SEM, TEM and XRD. Two kinds of LPSO structure were observed, include lamellar 14H-LPSO structure in the grain interior and chi phase at the grain boundaries. Lamellar 14H-LPSO structure in alpha-Mg matrix propagated in the matrix with the decease of solidification rate; and filled the whole grain in the alloy solidified at 0.005 degrees C/s. The second phase in the alloys also changed with deceasing the solidification rates; there are (Mg, Zn)(3)RE compounds only when solidification rate is 5 degrees C/s, (Mg, Zn)(3)RE compounds and 14H-LPSO structured chi phase when solidification rates are 0.5 and 0.1 degrees C/s, and 14H-LPSO structured chi phase only when solidification rates are 0.01 and 0.005 degrees C/s. It was detected that (Mg, Zn)(3)RE compounds and x phase existed simultaneously at the grain boundaries in the alloys at solidification rates of 0.5 degrees C/s and 0.1 degrees C/s, and the orientation relationship between them was determined to be [110](chi phase)//[(2) over bar 23]((mg,zn)3RE) and angle(001)(chi phase)(110)((mgzn)3RE)=8.4 degrees.

EFFECT OF COOLING RATE ON THE FORMATION OF 14H--LPSO STRUCTURE IN GWZ1032K ALLOY